OPTIMIZATION OF MECHANICAL PROPERTIES OF NANOSTRUCTURED ULTRALOW CARBON IF STEEL BY POST-PROCESS DEFORMATION

Naoya Kamikawa,Xiaoxu Huang,Niels Hansen

2009-01-01

Abstract:The effect of post-process annealing and deformation on mechanical properties was investigated in a nanostructured ultralow carbon interstitial free (IF) steel. Samples were produced by 6 cycles of accumulative roll-bonding (ARB), corresponding to a total thickness reduction of 98.4 %. The structure of the deformed samples contained closely-spaced high-angle boundaries, low-angle dislocation boundaries and individual dislocations in the volume between the boundaries. After annealing at 400 degrees C for 30 min, the yield stress and ultimate tensile strength increased and the elongation decreased. In contrast, an annealing treatment followed by a light rolling deformation up to 30 % thickness reduction led to a decrease in strength and a significant increase in elongation. Structural observation indicated that enhanced recovery takes place during a low-temperature annealing due to the narrowly-spaced high-angle boundaries that can act as sinks for dislocations and effectively remove dislocation sources. A higher stress may therefore be required to activate alternative dislocation sources in the annealed sample, and the re-introduction of dislocation sources by a subsequent rolling may lead to a lower stress required for dislocation activation and propagation and an increase in elongation. It is proposed that deformation instead of annealing can be a promising route to improve the ductility of nanostructured metals, and that a moderate light deformation can optimize the balance between strength and elongation.