Abstract:The ball milling technique has been successfully applied to the synthesis of various materials such as equilibrium intermetallic phases, amorphous compounds, nanocrystalline materials, or metastable crystalline phases. However, how the phase composition and nanoscale microstructure evolute during ball milling in various materials is still controversial due to the complex mechanism of ball milling, especially in the field of solid-state amorphization caused by ball milling. In the present work, the phase evolution during the high-energy ball milling process of the Mg and Cu (atomic ratio is 1:1) mixed powder was investigated. It was found that Mg firstly reacts with Cu, forming the Mg 2 Cu alloy in the primary stage of ball milling. As the milling time increases, the diffracted peaks of Mg 2 Cu and Cu gradually disappear, and only a broad halo peak can be observed in the X-ray diffraction pattern of the final 18-h milled sample. As for this halo peak, lots of previous studies suggested that it originated from the amorphous phase formed during the ball milling. Here, a different opinion that this halo peak results from the very small size of crystals is proposed: As the ball milling time increases, the sizes of Mg 2 Cu and Cu crystals become smaller and smaller, so the diffracted peaks of Mg 2 Cu and Cu become broader and broader and result in their overlap between 39° and 45°, at last forming the amorphous-like halo peak. In order to determine the origin of this halo peak, microstructure observation and annealing experiment on the milled sample were carried out. In the transmission electron microscopy dark-field image of the milled sample, lots of very small nanocrystals (below 20 nm) identified as Mg 2 Cu and Cu were found. Moreover, in the differential scanning calorimetry curve of the milled sample during the annealing process, no obvious exothermic peak corresponding to the crystallization of amorphous phase is observed. All the above results confirm that the broad halo diffracted peak in the milled MgCu sample is attributed to the overlap of the broadened peaks of the very small Mg 2 Cu and Cu nanocrystalline phase, not the MgCu amorphous phase. The whole milling process of MgCu can be described as follows: .

Effect of Ball-to-powder Weight Ratio on Microstructure Evolution of Nanocrystalline Mg-Zn Powders Prepared by Mechanical Milling

Effect of ball milling time on nanocrystalline powders and bulk ultrafine-grained Mg-3Al-Zn alloy

Effect of High Energy Milling on the Microstructure and Mechanical Properties of Mg-Zn-Zr Alloy

Effect of Ball Size on the Microstructure and Morphology of Mg Powders Processed by High-Energy Ball Milling

Microstructural Evolution of Mechanically Alloyed Mo–Si–B–Zr–Y Powders

Preparation of nanocrystalline magnesium alloy powders by high-energy ball milling

Effect of Processing Parameters on the Formation Process of Nano-Sized ZrB2 Powders by the High Energy Ball Milling

Mechanical effect of Mo powder in ball milling process

Mechanical Alloying Behavior of Nb–Ti–Si-based Alloy Made from Elemental Powders by Ball Milling Process

Microstructure And Mechanical Properties Of Nanocrystalline Al-Zn-Mg-Cu Alloy Prepared By Mechanical Alloying And Spark Plasma Sintering

The effects of the parameters of ball milling on the thermal stabilities of the as-milled MgNi amorphous

Effect of Ball Milling Parameters on Properties of Nano-Sized Tungsten Powder via Mechanochemical Processing

Effect of ball milling on the formation of Mg2Ni phase in sintering

EFFECTS OF BALL-MILLING INTENSITY ON STRUCTURAL-CHANGES IN MIXED 50NI-50TI POWDERS DURING MECHANICAL ALLOYING PROCESS

Effects of ball-milling intensity on the amorphization rate of mixed Ni50Ti50 powders

Investigation of phase composition and nanoscale microstructure of high-energy ball-milled MgCu sample

Microstructures And Mechanical Properties Of Nanocrystalline Az31 Magnesium Alloy Powders With Submicron Tib(2)Additions Prepared By Mechanical Milling

Effect of High-Energy Ball Milling in Ternary Material System of (Mg-Sn-Na)

Microstructures and Mechanical Properties of Nanocrystalline AZ31 Magnesium Alloy Powders with Submicron TiB2 Additions Prepared by Mechanical Milling

Effects Of Mechanical Ball Milling Time On The Microstructure And Mechanical Properties Of Mo2nib2-Ni Cermets

Mechanical properties of the Al-Mg/MWCNTs composite powders: The effects of ball milling process parameters