Influence of Nitrogen on Microstructure, Mechanical Properties and Martensitic Phase Transformation of Co–26Cr–5Mo–5W Alloys by Selective Laser Melting

Bo Wang,Xinglong An,Fei Liu,Min Song,Song Ni,Shaojun Liu

DOI: https://doi.org/10.1007/978-3-030-05861-6_40

2019-01-01

Abstract:The relationship between the microstructure, mechanical properties and martensitic phase transformation of N-containing Co–26Cr–5Mo–5W alloys by selective laser melting (SLM) is studied. The high-resolution transmission electron microscope and X-ray diffraction observations show that two phases (ε and γ phase) co-exist in N-free alloys. In contrast, a significant decrease of ε phase is observed in N-containing alloys. It is believed that the stabilization of γ phase in N-containing alloys results from the lattice distortion and Si-rich fine-distributed precipitates that block the motion of dislocations. Both the ultimate tensile strength and 0.2% proof strength can be significantly improved by nitrogen addition. Interestingly, the elongation slightly increases as well. They are ~1385 MPa, ~1140 MPa, and ~18.4% for 0.08 N-containing Co–26Cr–5Mo–5W alloys, respectively. It is clear that nitrogen addition during the SLM processing could be a promising strategy to fabricate Co–Cr–Mo–W alloys with an excellent combination of strength and ductility by suppressing face-centered cubic (fcc) → hexagonal close-packed (hcp) martensitic phase transformation.