Abstract:Currently, zinc has been considered as one new attractive biodegradable metal for medical implant applications due to its favoured properties such as biocompatibility and recycla-bility. However, the cast pure zinc usually possesses coarsening microstructures, which hinders it to obtain a suitable combination of mechanical strength and degradation rate. Here, the microstructural controlling of zinc was firstly realized via alloying dilute Mg contents and thermomechanical processing. Then, the in vitro biodegradation behaviour of dilute Zn-Mg alloys was investigated accordingly using the Hank's solution. Finally, the mechanisms of mechanical strengthening and in vitro biodegradation were explored. Specifically, the Mg-50wt%Zn master alloy was added into cast Zn melt to form the binary Zn-Mg alloys with different Mg addition contents (i.e. 0, 0.05wt%, 0.1wt%, and 0.4wt%). The initial reduction of grain sizes was achieved by over 90% owing to the grain refinement generated by master alloy. In the as-cast alloys, the average grain size was decreased from over 2 mm for pure Zn to 23.7 mm for Zn-0.4wt%Mg. Subsequently, the thermomechanical processing (i.e. hot rolling at room temperature, 100 degrees C, 150 degrees C, and 250 degrees C) was applied onto the cast Zn-Mg alloys to achieve further microstructural manipulation. Further grain refinement occurred in the different as-rolled Zn-Mg alloys. The in vitro corrosion resis-tance of all samples was assessed through the potentiodynamic polarization (PDP) test in the Hanks' solution for 14 days at 37 degrees C. The corrosion rates depended on alloying contents, grain sizes, twins and texture. The synergetic regulation of mechanical strength and degradation rate could be adjusted by appropriately using master alloys and thermo-mechanical processing. For practical medical applications, the present work provides some insights on solving the dilemma between mechanical properties and biodegradation process.(c) 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Influence Of Alloying Treatment And Rapid Solidification On The Degradation Behavior And Mechanical Properties Of Mg

Preparation and Characterization of Laser-Melted Mg–Sn–Zn Alloys for Biomedical Application

Microstructure Evolution And Biodegradation Behavior Of Laser Rapid Solidified Mg-Al-Zn Alloy

The Microstructure, Mechanical Properties and Degradation Behavior of Laser-Melted Mg-Sn Alloys

A combined strategy to enhance the properties of Zn by laser rapid solidification and laser alloying

Effect of Zn Concentration on the Microstructure and Mechanical Properties of Al-Mg-Si-Zn Alloys Processed by Gravity Die Casting

Effects of Zn Concentration and Heat Treatment on the Microstructure, Mechanical Properties and Corrosion Behavior of As-Extruded Mg-Zn Alloys Produced by Powder Metallurgy

Laser printed amorphous magnesium alloy: Microstructure, mechanical properties and degradation behavior

The Enhancement Of Mg Corrosion Resistance By Alloying Mn And Laser-Melting

Microstructure evolution and ductility improvement of additively manufactured biodegradable zinc–magnesium alloys via annealing

Effects of magnesium on microstructure, properties and degradation behaviors of zinc-based alloys prepared by selective laser melting

Biodegradation Mechanisms of Selective Laser-Melted Mg–xAl–Zn Alloy: Grain Size and Intermetallic Phase

A Novel Magnesium Alloy with Enhanced Mechanical Property, Degradation Behavior and Cytocompatibility

The Properties Evolution of Medical Mg–Zn Alloys Prepared by Semi-solid Powder Moulding

Novel Mg-based Alloys by Selective Laser Melting for Biomedical Applications: Microstructure Evolution, Microhardness and in Vitro Degradation Behaviour

Effects of thermomechanical processing on microstructures, mechanical properties, and biodegradation behaviour of dilute Zn-Mg alloys

Additive manufacturing of biodegradable Zn-xMg alloys: Effect of Mg content on manufacturability, microstructure and mechanical properties

Effect of original grain size on microstructure and properties of extruded Mg-2Zn-0.2Mn biomedical alloy

Selective Laser Melting of Mg-Zn Binary Alloys: Effects of Zn Content on Densification Behavior, Microstructure, and Mechanical Property

Effects of Al and Zn Contents on the Microstructure and Mechanical Properties of Mg-Al-Zn-Ca Magnesium Alloys

Research on an Mg-Zn alloy as a degradable biomaterial.