Elucidating the heat input on CGHAZ microstructure and its irregular effect on impact toughness for a novel V-N microalloying weathering steel
Bing Hu,Genhao Shi,Qiuming Wang,Liyang Zhao,Huibing Fan,Yucan Tang,Wei Wang,Qingfeng Wang,Riping Liu
DOI: https://doi.org/10.1016/j.jmrt.2023.07.086
IF: 6.267
2023-07-15
Journal of Materials Research and Technology
Abstract:This study investigated the effect of heat inputs on coarse-grained heat affected zone (CGHAZ) microstructure and impact properties of a novel vanadium (V) and nitrogen (N) microalloyed weathering steel via a Gleeble TM system, revealing the metallurgical essence of the steel suitable for large heat input ( E j ) welding. The results indicate that in CGHAZ, the dominant microstructure was composed of lath bainitic ferrite (LBF) at E j =15 kJ/cm, granular bainitic ferrite (GBF) at E j =35 kJ/cm, and a mixture of intragranular acicular ferrite (IGAF), intragranular polygon ferrite(IGPF) and grain boundary polygonal ferrite (GBPF) at E j =55 and 75 kJ/cm, respectively, apart from martensite/austenite (M/A) constituents in each one. The area fraction, f M/A , and mean size, d M/A , of M/A constituents increased monotonously with the E j . In addition, with increasing E j from 15 to 35 kJ/cm, the fraction, f MTAs>15° , of high-angle grain boundaries (HAGBs) with misorientation tolerance angles (MTAs) greater than 15° reduced, while the mean equivalent diameter, MED MTA≥15° , of grains with HAGBs increased. However, as E j further increased to 55 and 75 kJ/cm as the two large heat inputs, the precipitation of (Ti, V) (C, N) and thereby the heterogeneous nucleation of polygonal and acicular ferrite were promoted by a lowered degree of undercooling, resulting in the decreased MED MTA≥15° and the increased fraction f MTAs>15° . Accordingly, the impact toughness of CGHAZ was degraded with the increase of E j from 15 to 35 kJ/cm, but enhanced with the increase of E j from 35 to 75 kJ/cm.
materials science, multidisciplinary,metallurgy & metallurgical engineering