High Temperature Oxidation and Wear Behaviors of Ti-V-Cr Fireproof Titanium Alloy

Guangbao Mi,Kai Yao,Pengfei Bai,Congqian Cheng,Xiaohua Min

DOI: https://doi.org/10.3390/met7060226

IF: 2.695

2017-01-01

Metals

Abstract:The high temperature oxidation and wear behaviors of Ti-35V-15Cr-0.3Si-0.1C fireproof titanium alloy were examined at 873 and 1073 K. The oxidation weight gain after oxidation at 1073 K for 100 h was significantly larger than that at 873 K. Based on the analyses of the oxidation reaction index and oxide layer, the oxidation process at 1073 K was mainly controlled by oxidation reaction at the interface between the substrate and oxide layer. Dry sliding wear tests were performed on a pin-on-disk tester in air conditions. The friction coefficient was smaller at 1073 K than that at 873 K, while the volume wear rate at 1073 K was larger due to formation of amount of oxides on the worn surface. When the wearing temperature increased from 873 to 1073 K, the wear mechanism underwent a transition from a combination of abrasive wear and oxidative wear to only oxidative wear.