Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Effect Of Temperature Scheme On Microstructure And Mechanical Properties During Medium Carbon Steel Warm Processing

Effects of Warm Rolling Temperature on Microstructure Evolution and Mechanical Properties of Medium Carbon Martensite Steel

Effect of Cooling Mode on the Microstructure and Mechanical Properties of Medium Carbon Steel after Warm Rolling

Influence of warm rolling temperature on multi-scale lamellar structure and mechanical properties of medium carbon steel

Effect of Warm Rolling Temperature on the Microstructure and Texture of Microcarbon Dual-Phase (DP) Steel

Microstructure Evolution and Mechanical Properties of Medium Carbon Martensitic Steel during Warm Rolling and Annealing Process

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Effect of Warm Rolling Process Parameters on Microstructure and Mechanical Properties of Structural Steels

Effect of Time Interval on Microstructure Evolution of Medium Carbon Steel During Warm Deformation

Microstructural Evolution and Mechanical Properties of 6cr13 Martensitic Stainless Steel Subjected to Cold Rolling and Heat Treatments

Effect of Deformation Temperature on Microstructure Evolution and Mechanical Properties of Low-Carbon High-Mn Steel

Microstructure Evolution of Medium Carbon Martensite Steel During Warm Rolling and Annealing

Microstructure evolution and compressive properties of a low carbon-low alloy steel processed by warm rolling and subsequent annealing

Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel

Effects of Annealing Process on Microstructure and Mechanical Properties of Hot Rolled Medium Carbon Steel Plate

Effects of Annealing Time on Microstructure Evolution of Bidirectional Warm Rolled Medium Carbon Martensite Steel

Microstructure evolution and mechanical properties of metastable austenitic medium Mn steel fabricated by warm caliber rolling

Mechanical Properties of Plain Carbon Steels with Ultrafine (α+θ) Microstructures

Effect of Deformation on Microstructure and Mechanical Properties of Medium Carbon Steel During Heat Treatment Process

INFLUENCE OF DEFORMATION TEMPERATURE ON THE MICROSTRUCTURE TRANSFORMATION IN MEDIUM CARBON STEEL

Effect of Different Strain on Microstructure Evolution of Medium Carbon Steel