Effects of Annealing Process on Microstructure and Mechanical Properties of Hot Rolled Medium Carbon Steel Plate

Dengcui YANG,Yunli FENG,Xiaojing WANG

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.20.066

2017-01-01

Abstract:The influences of different annealing holding time on spheroidization of the carbide, recovery and recrystallization of ferrite, mechanical properties of experimental steel were studied by using SEM and EBSD analytical techniques. The results show that, after hot rolling of experimental steel, and air cooling to 650 ℃, and then annealing for different time, when the holding time is 30 min, the recrystallization of most of the ferrite occurs and the ferrite grain size is the smallest (about 7 μm). The yield strength and tensile strength of hot rolled steel are higher, which are 570 MPa and 725 MPa, respectively, while the elongation rate is 13％. When the hot rolling steel sample is cooled to 650 ℃ and annealing for 30min, the tensile strength and yield strength decrease significantly, dropping to 460 MPa and 635 MPa, and the elongation significantly increases, reaching 21％.