Abstract:1.4 %C ultra high carbon steel (UHCS) was prepared in order to study the structure of martensite transformation and mechanical properties. Ultra-fine spherical carbide and ultra-fine austenite grain size were obtained. A great deal of lath martensite was observed after quenching. The phenomenon does not agree with the traditional knowledge that the lath martensite would disappear when carbon content is in excess of 0.8% in austenite. The strength, fatigue properties and fracture toughness have been measured. A good combination of strength, toughness and fatigue properties come from fine and uniform distributed carbide particles and ultra-fine austenite grain size. Fracture strength increases by 48%, yield strength increases by 15% and plasticity keep the same comparing with that of hardened and tempered 40CrNiMo. The carbon content of ultrahigh carbon steels (UHCS) is in the range of 1.0-2.1% [1, 2]. Traditional heat treatments for normal steels will cause the microstructure of UHCS to be coarse and do not produce optimal properties. With controlled rolling and special heat treatment, UHCS can be in ferrite, pearlite, bainnite or martensite structures, which all have different mechanical properties. The yield stress of a 1.8%C, 1.6%Al ferrite UHCS can reach 1500MPa, which is much higher than that of high strength and plain alloy steels [3]. The tensile strength of a 1.25%C-1.5%Cr pearlite UHCS can reach 1810Mpa and its elongation can be 18%. When it is treated into martensite, its compression strength reached to 4690Mpa and compression strain reached to 26% [1, 4], which is comparable to WC-12Co. Such good mechanical properties can be ascribed to the ultra fine grain sizes because of the undissolved carbide particles which resist growth of austenite grain during heating. Another reason could be the lath martensite structures. O.D.Sherby [4] had reported that there was a lot of lath martensite in quenched UHCS. The UHCS was considered not only as tool steels but also as good structure materials. Fracture and fatigue properties are important for structure materials. However, they have rarely been studied. The present paper is going to study the martensite structure and mechanical properties of a prepared 1.4% C UHCS.

Mechanical Properties of Plain Carbon Steels with Ultrafine (α+θ) Microstructures

Enhancement of mechanical properties by changing microstructure in the eutectoid steel

Microstructure Evolution and Mechanical Properties of Eutectoid Steel with Ultrafine or Fine (ferrite+cementite) Structure

Relationship between microstructure and yield strength for plain carbon steel with ultrafine or fine (ferrite+cementite) structure

Mechanical Properties of Hypereutectoid Steel with Microduplex (α+θ) Structure Formed by Hot Deformation of Undercooled Austenite

Microstructure and mechanical properties of high-carbon Si-Al-rich steel by low-temperature austempering

Microstructure Evolution and Mechanical Properties of Medium Carbon Martensitic Steel during Warm Rolling and Annealing Process

Microstructure Evolution of a Pearlitic Steel during Hot Deformation of Undercooled Austenite and Subsequent Annealing

Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing

Ultrafined microstructure of hypereutec-toid steel by warm deformation of martensite

Achieving Fine-Grained Microstructure and Superior Mechanical Property in a Plain Low-Carbon Steel Using Heavy Cold Rolling Combined with Short-Time Heat Treatment

Microstructure Evolution and Properties of Q235 Plain Carbon Steel in Multi-pass Hot Deformation

Enhanced mechanical properties of a high-carbon martensite steel processed by heavy warm rolling and tempering

Microstructure and Mechanical Properties of A Ultra-High Carbon Steel

Microstructure and properties of ultrafine grained ultrahigh carbon (1.73 Pct C) steel

Microstructure and Properties of 1.6%C Ultra-high Carbon Steel

An Investigation on the Microstructure and Mechanical Properties in an Ultrafine Lamellar Martensitic Steel Processed by Heavy Warm Rolling and Tempering

Effect of Fine Cementite Particles on Tensile Properties of Carbon Steel after Warm Rolling and Annealing

Microstructures and Mechanical Properties of Ferrite-Based Lightweight Steel with Different Compositions

Microstructure and Mechanical Properties of A 1.4%C Ultra High Carbon Steel

Mechanical Properties of an Ultra-high Carbon Steel