Research on AlSi7Mg Alloy Semi-Solid Billet Fabricated by RAP
Jiang Jufu,Zhang Yihao,Liu Yingze,Wang Ying,Xiao Guanfei,Zhang Ying
DOI: https://doi.org/10.11900/0412.1961.2020.00254
IF: 1.797
2021-01-01
ACTA METALLURGICA SINICA
Abstract:Semi-solid metal processing is a metal-forming technology that combines the advantages of casting and forging, realizing near-net forming high-performance parts with complex structures. Research on semi-solid processing of AlSi7Mg alloys mainly focuses on rheology, and the preparation of high solid fraction AlSi7Mg semi-solid billets by the solid phase method has been largely neglected. In fact, semi-solid technology is more significant than casting at higher solid fractions. The present study investigates semi-solid billets of AlSi7Mg aluminum alloy with a high solid fraction, prepared by the recrystallization and partial re-melting (RAP) method. The effects of upsetting temperature, compression ratio, semi-solid isothermal treatment temperature, and holding time on the billet microstructure were investigated by DSC test, upsetting experiment, semi-solid isothermal treatment experiment, OM observations, and Image Pro Plus image processing software. The microstructure of the semi-solid billet during isothermal compression was slightly affected by temperature but was beneficially refined by increasing the compression ratio. The optimal hot upsetting parameters were 240 degrees C and 40% deformation. During the semi-solid isothermal treatment, increasing the holding temperature gradually increased the size of the solid phase grains in the microstructure. As the holding time increased, the solid phase particles in the semi-solid structure initially grew slowly, and thereafter rapidly grew to a stable size. The changes in roundness of the solid particles were more complicated. The average grain size of the billet prepared by the RAP method was 64 similar to 117 mu m, and the shape factor was 0.76 similar to 0.89. The linear relationship between cubic coarsening of the average semi-solid grain size and isothermal time was nonobvious at isothermal temperatures below 599 degrees C but was evident at temperatures of 599 degrees C. Below 599 degrees C, the grain coarsening is affected by Ostwald ripening, coalescence, recrystallization, and melting; while at 599 degrees C, the grain coarsening was dominated by Ostwald ripening.