Abstract:In this study, a large-area superhydrophobic alumina surface with a series of superior properties was fabricated via an economical, simple, and highly effective one-step anodization process, and subsequently modified with low-surface-energy film. The effects of the anodization parameters including electrochemical anodization time, current density, and electrolyte temperature on surface morphology and surface wettability were investigated in detail. The hierarchical alumina pyramids-on-pores (HAPOP) rough structure which was produced quickly through the one-step anodization process together with a low-surface-energy film deposition [1H,1H,2H,2H-perfluorodecyltriethoxysilane (PDES) and stearic acid (STA)] confer excellent superhydrophobicity and an extremely low sliding angle. Both the PDES-modified superhydrophobic (PDES-MS) and the STA-modified superhydrophobic (STA-MS) surfaces present fascinating nonwetting and extremely slippery behaviors. The chemical stability and mechanical durability of the PDES-MS and STA-MS surfaces were evaluated and discussed. Compared with the STA-MS surface, the as-prepared PDES-MS surface possesses an amazing chemical stability which not only can repel cool liquids (water, HCl/NaOH solutions, around 25 °C), but also can show excellent resistance to a series of hot liquids (water, HCl/NaOH solutions, 30-100 °C) and hot beverages (coffee, milk, tea, 80 °C). Moreover, the PDES-MS surface also presents excellent stability toward immersion in various organic solvents, high temperature, and long time period. In particular, the PDES-MS surface achieves good mechanical durability which can withstand ultrasonication treatment, finger-touch, multiple fold, peeling by adhesive tape, and even abrasion test treatments without losing superhydrophobicity. The corrosion resistance and durability of the diverse-modified superhydrophobic surfaces were also examined. These fascinating performances makes the present method suitable for large-scale industrial fabrication of chemically stable and mechanically robust superhydrophobic surfaces.

Drag-reductive and Anti-Corrosive Superhydrophobic Surface Fabricated on Aluminum with Thin PDMS/SiO2coating

Spray-coated Superhydrophobic Surfaces with Wear-Resistance, Drag-Reduction and Anti-Corrosion Properties

Fabrication of Air-Permeable Superhydrophobic Surfaces with Excellent Non-Wetting Property

Facile and Fast Fabrication Method for Mechanically Robust Superhydrophobic Surface on Aluminum Foil

Fabrication of Superhydrophobic Aluminum Surface by Droplet Etching and Chemical Modification

Chemically Stable and Mechanically Durable Superamphiphobic Aluminum Surface with a Micro/Nanoscale Binary Structure

Robust superhydrophobic film on aluminum alloy prepared with TiO 2 /SiO 2 -silane composite film for efficient self-cleaning, anti-corrosion and anti-icing

Superhydrophobic Self-Assembled Silane Monolayers on Hierarchical 6082 Aluminum Alloy for Anti-Corrosion Applications

Fabrication of superhydrophobic aluminum alloy surfaces by nickel and phosphorus chemical deposition

Highly Efficient and Large-Scale Fabrication of Superhydrophobic Alumina Surface with Strong Stability Based on Self-Congregated Alumina Nanowires

Fabrication of Stable Superhydrophobic Surface with Low Adhesion on Aluminum Foil

Fabrication of a Highly Stable Superhydrophobic Surface with Dual-Scale Structure and Its Antifrosting Properties

HD-SiO2/SiO2 Sol@PDMS Superhydrophobic Coating with Good Durability and Anti-Corrosion for Protection of Al Sheets

Robust and Chemically Stable Superhydrophobic Aluminum-Alloy Surface with Enhanced Corrosion-Resistance Properties

Fabrication of Superhydrophobic Surface on Anodized Aluminum Through a Wet-Chemical Route

Wetting Behavior and Drag Reduction of Superhydrophobic Layered Double Hydroxides Films on Aluminum

Nano-SiO2 Based Anti-Corrosion Superhydrophobic Coating on Al Alloy with Mechanical Stability, Anti-Pollution and Self-Cleaning Properties

Fabrication of superhydrophobic surfaces with hierarchical structure and their corrosion resistance and self-cleaning properties

Superhydrophobic surfaces created by a one-step solution-immersion process and their drag-reduction effect on water

A facile and cost-effective fabrication of robust carbon black-based superhydrophobic coatings on aluminum alloy