Abstract:Squeeze casting process can effectively resolve the casting difficulties for wrought aluminum alloys by pressurized solidification. The effects of applied pressure (0.1-125 MPa) on the microstructure refinement, non-equilibrium eutectic phase aggregation and fracture behavior of Al-Zn-Mg-Cu alloys prepared by squeeze casting were investigated through metallography, scanning electron microscopy and energy dispersive spectroscopy. The results showed that the primary α-Al grains transformed from coarse dendrites to refined equiaxed grains with increasing pressure. Considerable primary refinement was achieved at 100 MPa, with a significant decrease by 63% in the average grain size from 273 μm to 101 μm; the non-equilibrium eutectic phases were homogenized and refined, and almost dissolved into the Al matrix after T6 heat treatment. The mechanism of solidification behaviors in pressurized solidification was elucidated. Firstly, the applied pressure increased the thermodynamic driving force to promote primary grain nucleation. Secondly, the solute diffusion and constitutional undercooling at the front of the solid/liquid interface front were inhibited by pressure, and grain growth in a dendritic structure was thus restrained. Thirdly, interdependence theory and thermodynamic calculations were conducted to quantitatively describe the primary grain size changes under pressurized solidification. Lastly, the ternary eutectic reaction L → α-Al + T-Mg (Al, Zn, Cu) 2 + Al 2 Cu and binary eutectic reaction L→ α-Al + Al 7 Cu 2 Fe were suppressed by the reduced solute segregation. Furthermore, when the pressure increased from 0.1 MPa to 125 MPa, the ultimate tensile strength was raised from 428 MPa to 538 MPa, almost approaching that of samples by forging process. The refined eutectic phases decreased stress concentration and improved fracture behaviors.

Effect of Holding Pressure on Microstructure and Fracture Behavior of Low-Pressure Die Cast A356-T6 Alloy

Effect of Holding Pressure on Microstructure and Mechanical Properties of A356 Aluminum Alloy

Effects of different holding pressures on the microstructure and mechanical properties of Al-5.9Zn-2.2Mg-1.8Cu alloy

Effect of Heat Treatment on Microstructures and Mechanical Properties of A356 Alloy by Low Pressure Casting

Effect of Forging Pressure on Microstructure and Mechanical Properties of 6061 Alloy Prepared by Casting-Forging Compound Forming

Study on tensile properties and fractography of cast A356 aluminum alloy

Microstructure and Mechanical Properties of a 6061 Aluminum Alloy Part Prepared by Casting-Forging Integrated Forming Technology

The Effect of Hot Isostatic Pressing on the Microstructure and Tensile Properties of an Unmodified A356-T6 Cast Aluminum Alloy

Effect of Chemical Compositions on Tensile Behaviors of High Pressure Die-Casting Alloys Al-10si-Ycu-Xmn-Zfe

Tensile Properties and Deformation Behaviors of a New Aluminum Alloy for High Pressure Die Casting

Characterization of high-pressure die-cast hypereutectic Al-Si alloys based on microstructural distribution and fracture morphology

The effect of different high pressure die casting parameters on 3D microstructure and mechanical properties of AE44 magnesium alloy

Effect of pressure on the microstructure refinement, solidification mechanism and fracture behavior of wrought Al-Zn-Mg-Cu alloys prepared by squeeze casting

On the characterization of microstructure and fracture in a high-pressure die-casting Al-10 <i>wt</i>%Si alloy

Microstructure, Tensile Properties and Fractography of A356 Alloy under As-Cast and T6 Obtained with Expendable Pattern Shell Casting Process

Fracture Behavior of a High Pressure Die Casting AlSi10MnMg Alloy with Varied Porosity Levels

Characteristics of Mold Filling and Entrainment of Oxide Film in Low Pressure Casting of A356 Alloy

Effect of Pressure on Microstructures and Mechanical Properties of Al-Cu-based Alloy Prepared by Squeeze Casting

Microstructure and Tensile Properties of Cast A356 Aluminum Alloy

Correlation of Microstructure with Mechanical Properties and Fracture Behavior of A356-T6 Aluminum Alloy Fabricated by Expendable Pattern Shell Casting with Vacuum and Low-Pressure, Gravity Casting and Lost Foam Casting

Strengthening Mechanisms and Work Hardening in a Heterostructured Cast Aluminum Alloy under Compressive Loading: Correlation with Nanomechanical Properties