Tensile Properties and Deformation Behaviors of a New Aluminum Alloy for High Pressure Die Casting

Peng Zhang,Zhenming Li,Baoliang Liu,Wenjiang Ding,Liming Peng

DOI: https://doi.org/10.1016/j.jmst.2016.02.013

IF: 6.044

2015-01-01

Materials Science and Engineering A

Abstract:This paper investigates the effects of strain rate and test temperature on the tensile properties and deformation behavior of a recently developed high-ductility cast aluminum alloy Al–5Mg–0.6Mn. The as-cast alloy tested at room temperature and the lowest strain rate of ~1.67×10−4s−1 shows the highest yield strength of ~212MPa, ultimate tensile strength of ~357MPa and elongation (~17.6%). Increasing strain rate reduces the ultimate tensile strength and ductility of the as-cast alloy. With the increasing of test temperature, the as-cast alloy shows significantly decreases in tensile strengths and improvements in elongation. The tensile failure of the alloy is mainly originated from the cracking and debonding eutectic particles. The Portevin–Le Chatelier effect occurs in the alloy tested at RT. Strain rate in current study ranges does not significantly affect the work-hardening behavior of the alloy. Increasing test temperature apparently reduces the strain-hardening exponent and coefficient. For the alloy tested at RT, all tensile failures occur prior to global instability, indicating the existence of localized damage. In contrast, for the alloy tested at HT, the global instability occurs at strains below the logarithmic fracture strains, suggesting that there is still a postnecking damage.