Interfacial Morphologies and Corrosion Behaviours of Novel Fe-Cr-B Alloys Immersed in Molten Aluminium

Zicheng Ling,Weiping Chen,Xin Yang,Bing Li,Tiwen Lu
DOI: https://doi.org/10.1088/2053-1591/aafeb1
IF: 2.025
2019-01-01
Materials Research Express
Abstract:In aluminium industry, the molten aluminium and its alloys have a serious attack to the holders and the contact instruments, and therefore forming a layer Fe-Al intermetallic compounds (IMCs), which leads to relative mass loss or even failure. For this question, three kinds of Fe-Cr-B alloys were prepared and their interfacial morphologies and corrosion behaviours immersed in static molten aluminium at 750 °C were systematically investigated using SEM, XRD and TEM. The results showed that the M2B-type boride phase had the excellent corrosion resistance property, especially the coarse rod-like Cr-rich M2B boride. Additionally, the periodic layered structures (PLSs) produced from the corroded rod-like Cr-rich M2B boride, which could not only retard the reaction diffusion of Al atoms and matrix but also reduce the Fe-Al IMCs spallation. The corrosion behaviour of Fe-Cr-B alloy was mainly the corrosion of matrix, the formation and the spallation of Fe-Al IMCs and the degradation of boride phase. Notably, the volume loss rate of the Fe-13.54 wt% Cr-3.88 wt% B alloy, was 78% lower than that of H13 steel.
What problem does this paper attempt to address?