The effect of stress rate on ratchetting behavior of rolled AZ31B magnesium alloy at 393K and room temperature

Li Meng,Simon Hallais,Alexandre Tanguy,Wufan Chen,Miaolin Feng

DOI: https://doi.org/10.1088/2053-1591/ab19e9

IF: 2.025

2019-01-01

Materials Research Express

Abstract:To study the rate effect on the ratchetting behavior of rolled AZ31B magnesium (Mg) alloy at 393 K and room temperature, stress-controlled cyclic tension-compression experiments using various load rates were conducted. Four loading amplitudes with different mean stresses were used to study the roles of dislocation slipping and twinning/detwinning in different plastic deformation mechanisms. The ratchetting of the AZ31B Mg alloy was found to be temperature dependent, as the accumulated plastic strain increased as temperature increasing. Furthermore, ratchetting was more apparent at 393 K than at room temperature, especially under higher loading amplitudes with larger tension peak stresses. The rate effect on ratchetting was temperature sensitivity. That is, ratchetting was rate sensitive at 393 K, but was rather rate insensitive at room temperature, as the slops of the peak and valley strain varied with different load rate at 393 K. The mechanisms of different hysteresis loops, the rate effects on peak and valley strains and the 'ratchetting recovery' phenomenon are discussed.