Abstract:Rapid heat treatment is an important method to improve the properties of steel. Moreover, the study of the phase transformation process plays an important role in the formulation of rapid heat treatment. This paper investigates phase transformation behavior and microstructure evolution of ultrafine bainite at varying heating rates, and reveals the influence mechanism of retained austenite on austenitizing. Results showed that the decomposition of retained austenite was influenced by the diffusion of Si element. Therefore, the decomposition temperature of retained austenite is severely affected by the heating rate. Retained austenite completely transformed into cementite and ferrite when heating rate was below 5 degrees C/s. A small amount of retained austenite was kept when the heating rate was higher than 5 degrees C/s. The kept austenite effectively suppressed the hysteresis of Ac1 and resulted in a unique mechanism of austenite grain formation. When the heating rate range was 5-10 degrees C/s, some new austenite skipped the nucleation process and grew directly on the kept austenite, forming the large austenite grains. And other new austenite was obtained via nucleation and growth process. Thus, the grain size of bimodal distribution is formed. This leads to the phenomenon of austenite memory effect. When the heating rate was increased to 50 degrees C/s and higher, the austenite grain size was less than 14 mu m. Therefore, rapid heating makes the phase transition lag. When the heating rate is high enough, part of the austenite is kept, which has an important influence on austenitizing process of the steel.

A Special Phase Transformation Phenomenon in High-Nitrogen Austenite

A Special Phase Transformation Phenomenon in High Degree of Supersaturation Nitrogenous Supercooled Austenite

Isothermal transformation of high-nitrogen austenite

Research on Mediate Temperature Decomposition of High Nitrogen Austenite

Intermediate Temperature Transformation of the High-nitrogen Austenite

Mediate Temperature Transformation on Grain Boundaries of High-Nitrogen Austenite

In-situ Observation of Phase Transformation During Heat Treatment Process of High-Carbon Bainitic Bearing Steel

Microstructure and Characterization of High Hardness Produced in High-Nitrogen Austenite Intermediate Temperature Transformation

Inversion of Nitrogen Redistribution in Austenitic Steel by Severe Plastic Deformation

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel

Inner connection of bainite and pearlite transformation in steels

Kinetic Transitions and Mn Partitioning During Austenite Growth from a Mixture of Partitioned Cementite and Ferrite: Role of Heating Rate

Isothermal decomposition behavior of the high nitrogen concentration γ-Fe[N] prepared from pure iron

Research on the Phase Transformation of a Newly Developed Carbonitride-Strengthened Martensitic Heat Resistant Steel

Splitting Phenomenon in Martensitic Transformation of X12crmowvnbn10-1-1 Steel

Morphology and Crystallographic Orientation Relationship in Isothermally Transformed Fe–N Austenite

Evolution of ultrafine bainite microstructure during rapid heating process and the role of retained austenite

Real-time Observation of Bainite Formation at Heterogeneous Phases in a High-Strength Weathering Steel

Isothermal Transformation of Low Temperature Super Bainite

Apparent Morphology and Structure of Martensite in Ultrahigh Carbon Steel

Partition and Non-Partition Transition of Austenite Growth from a Ferrite and Cementite Mixture in Hypo- and Hypereutectoid Fe-C-Mn Alloys