Abstract:Due to the various structural and functional characteristics of lightweight, energy absorption and sound/heat insulation et al, metallic foam materials have been increasingly developed in recent years, especially for the most widely used alloy foams. In this work, the Al‐Mg‐Si alloy foams with a porosity of 60% were prepared by a powder metallurgy technology, in which the carbamide was used as the space‐holder material. The effect of solution treatment on the microstructure, compressive property and energy absorption response of the as‐prepared Al‐Mg‐Si alloy foams was studied. The results show that when the solution temperature (T) is increased from 25 to 555 ℃, the room‐temperature compressive strength of the Al‐Mg‐Si alloy foams increases from 11.2 to 26.7 MPa, but decreases when T is more than 555 ℃. The strengthening mechanisms of solution treatment mainly lie in that the dislocation movement between the grain boundaries can be effectively blocked by the precipitated phases. Regarding to the high‐temperature compressive property of the Al‐Mg‐Si alloy foams that solution‐treated at 555 ℃, the compressive strength is found decrease from 28.7 to 12.3 MPa when the compression temperature is elevated up to 250 ℃. Correspondingly, the energy absorption decreases from 17.02 to 9.14 MJ/m3. Compared to the pure Al foam, the high‐temperature softening effect for the Al‐Mg‐Si alloy foams is more remarkable, which ascribes to the formation of microcracks in the alloy matrix. The current research provides us a cost‐effective and easy‐handle approach to enhance the compressive strength and energy absorption ability of the metallic foam materials.This article is protected by copyright. All rights reserved.

Effect of Aging Treatment on the Quasi-Static and Dynamic Compressive Properties of Aluminum Alloy Foams

Effect of Aging Treatment on the Dynamic Compressive Property and Energy Absorption Capacity of Aluminum Alloy Foams

Strain rate effects on the compressive property and the energy-absorbing capacity of aluminum alloy foams

Effect of aging treatment on the microstructure and flow behavior of 6063 aluminum alloy compressed over a wide range of strain rate

Compressive Properties and Energy Absorption of Aluminum Foams with a Wide Range of Relative Densities

Mechanical Properties of Aluminium Foam and How Density, Temperature, and Strain Rate Affect Dynamic Strain–Stress Relationship

Effect of Heat Treatment on the Microstructure, Compressive Property, and Energy Absorption Response of the Al–Mg–Si Alloy Foams

Study on Quasi-Static Compressive Properties of Aluminum Foam-Epoxy Resin Composite Structures

Effect of aging treatment on microstructure, mechanical and corrosion properties of 7055 aluminum alloy prepared using powder by-product

Quasi-static and High Strain Rates Compressive Behavior of Aluminum Matrix Syntactic Foams

Quasi-static Deformation Mechanism and Compressive Properties of Aluminum Foams Fabricated by Friction Stir Processing

Effect of Artificial Aging, Delayed Aging, and Pre-Aging on Microstructure and Properties of 6082 Aluminum Alloy

Homogeneous Age-hardening of Large-sized Al-Sc Foams via Micro-alloying with Zr and Ti

Effects of under-aging treatment on microstructure and mechanical properties of squeeze-cast Al-Zn-Mg-Cu alloy

Anisotropic Compressive Behavior of Functionally Density Graded Aluminum Foam Prepared by Controlled Melt Foaming Process

The effect of aging treatment on the microstructure and properties of a crystallite (2024Al)-20Si-5Fe alloy

Influence of aging treatment on mechanical properties of 6061 aluminum alloy

Effects of different initial states on dynamic tensile properties and microstructure of 7075 aluminum alloy

Dynamic mechanical properties of aluminum alloy foams

Effect of Aging Treatment on Tensile Behaviors of Cast Mg-9Gd-4Y-0.5Zr Alloy

Effect of the interfacial reaction of aluminum and yttrium oxide on aging behavior of aluminum–magnesium–silicon alloy reinforced with yttrium oxide modified sub-micron alumina