Abstract:To consider the acceleration effect induced by the underloads in the design stage, the fatigue crack growth rates in S355 steel were measured based on the compliance method. Three different load sequences, constant amplitude loading (CAL), single underload (UL), and periodic underloads (PULs), were tested. Moreover, several methods were used to study the relevant mechanisms from the macroscopic and microscopic perspectives, including the digital image correlation technique, X-ray diffraction, transmission electron microscopy, and finite element method, etc. Compared with the crack growth during CAL, the UL induced a notable crack growth acceleration in subsequent cyclic loadings. When the amplitude of UL was constant, the effect of UL enhanced with the lower stress ratio of the fatigue baseline loading. In the macroscopic view, the acceleration effect was primarily attributed to the decreasing plasticity-induced crack closure and induced tensile residual stress at the crack tip. A higher amplitude underload led to an increase in the crack acceleration, which gradually degenerated within the following cycles. The PULs were also affected by the amplitude of underloads. The relevant crack growth acceleration mechanisms were closely related to the cycles affected by UL and the crack opening level. Another main parameter affecting PULs was associated with the number of cycles between two consecutive underloads: the frequency of PULs, which reflects the degree of interaction and accumulation. In the microscopic view, the accumulation of dislocation around the crack tip induced by PULs contributed to the crack acceleration, along with the corresponding periodic striations in the fractography. This study showed the crack growth acceleration effect caused by underloads and demonstrated the interactions between the UL and PULs, offering a better understanding of the acceleration mechanisms.

Investigation of Fatigue Crack Growth under Loading Sequence Effects Using In-Situ SEM Testing

In-situ SEM and Optical Microscopy Testing for Investigation of Fatigue Crack Growth Mechanism under Overload

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

In-Situ SEM Testing for Transient Fatigue Crack Growth Behavior Investigation Subjected to a Single Tensile Overload

Investigation of Incremental Fatigue Crack Growth Mechanisms Using in Situ SEM Testing

Investigative Method for Fatigue Crack Propagation Based on a Small Time Scale.

In Situ SEM Testing for Crack Closure Investigation and Virtual Crack Annealing Model Development

In-Situ Fatigue Crack Growth Testing of Al7075-T651 under Scanning Electron Microscopy

In-situ Experimental Investigation and Prediction of Fatigue Crack Growth for Aluminum Alloys under Single Spike-Overloads

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

Application of Strain Energy Based Approach for Evaluation of Fatigue Crack Growth Retardation Effect under Random Overload

Effect of Crack-Tip Deformation on Fatigue Crack Growth: A Comparative Study under Overload/underload Conditions

In situ SEM fatigue testing technology for metallic materials: a review

Subcycle Fatigue Crack Growth Mechanism Investigation for Aluminum Alloys and Steel

Fatigue Crack Growth Behavior of Marine Steel under Variable Amplitude Loading-Combining DIC Technique and SEM Observation

On the Study of Fatigue Crack Propagation in the Time Domain

Preliminary Experimental Investigation of Loading Sequence Effects on Low-Cycle Bending Fatigue

Semi-quantitative creep-fatigue damage analysis based on diffraction-based misorientation mapping and the correlation to macroscopic damage evolutions

In situ SEM-DIC technique and its application to characterize the high-temperature fatigue crack closure effect

Fatigue Crack Growth Acceleration in S355 Steel under a Single and Periodic Underload

Investigation of Fatigue Growth Behavior of an Inclined Crack in Aluminum Alloy Plate