Thermal behaviors of kaolinite-diasporic bauxite and desilication from it by roasting-alkali leaching processing

T Jiang,GH Li,ZC Huang,XH Fan,GZ Qiu

2002-01-01

Abstract:By means of XRD, TG and DTA techniques, the thermal behaviors of kaolinite-diasporic bauxite are investigated in this paper. Results show that the kaolinite in the bauxite loses its constitutional water and turns into meta-kaolinite when temperature is elevated above 450degreesC. The meta-kaolinite is decomposed into amorphous silica and non-crystal alumina in the range of 990-1100 degreesC, but latter two compose into mullite if the temperature exceeds 1100 degreesC. It is found that diaspore is changed into cc-alumina with the removal of its constitutional water at the temperature over 650 degreesC. A desilication process of roasting-alkali leaching for the bauxite is developed on the basis of the results. The optimum roasting parameters are attained to be a grain size of 0similar to20mm, a roasting temperature of 1050-1100degreesC, and a roasting time of 15-20 minutes. The proper leaching conditions are found as 100 g/l Na2Ok and 1400 degreesC. By alkali leaching of the roasted bauxite, a concentrate of 9.92 A/S ratio is achieved for a raw bauxite ore with a 4.4 A/S ratio. It is found the silica removed by the roasting-alkali leaching processing is mainly the amorphous silica and the reaction of mullitization causes reduction in desilication. The a-alumina yielded by diaspore decomposition during roasting is not dissolved under the alkali leaching conditions. The Bayer leaching tests of the concentrate show that the desilication by roasting-alkali leaching processing improves the digestion properties of Al2O3 in the bauxite.