Desilication of Coal-Derived Pyrite Flotation Tailing for Preparing Alumina Concentrate by Thermochemical Activation Process
LUO Jun,LI Guang-hui,RAO Ming-jun,ZHANG Ji-qing,GUO Yu-feng,JIANG Tao
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2013.12.028
2013-01-01
The Chinese Journal of Nonferrous Metals
Abstract:Aiming at preparing alumina concentrate from coal-derived pyrite flotation tailing, a desilication technique using thermochemical activation process followed by alkali leaching was proposed, and the suitable processing parameters and desilication mechanism were investigated. The results show that the optimal thermochemical activation processing parameters are as follows: roasting temperature 1 150 ℃, roasting time 15-20 min, alkali leaching temperature 125-140 ℃, leaching time 30 min and NaOH concentration 140 g/L. In this case, an alumina concentrate with 69.29%Al2O3 and mass ratio of alumina to silica (A/S) of 5.59 is obtained from a pyrite flotation tailing bearing 46.22%Al 2 O 3 and 28.33%SiO 2 (mass fraction), and the corresponding desilication ratio is 71.91%. XRD results show that aluminosilicates of the pyrite flotation tailing, including illite-montmorillonite, kaolinite and pyrophyllite, are decomposed into amorphous SiO 2 and small amount of mullite after thermochemical activation. Meanwhile, diaspore is transformed intoα-Al 2 O 3 . During the alkali leaching of activated materials, amorphous SiO 2 dissolves in the caustic soda, while mullite and α-Al2O3 do not dissolve, and the formation of sodium aluminosilicate hydrate (Na8Al6Si6O24(OH)2(H2O)2 ) during leaching leads to a decrease of desilication. Otherwise, rutile from thermal transformation of portion anatase, as well as hematite from oxidation, is not capable of being dissolved in alkali solution and shifted to alumina concentrate.