Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Tuning Nanostructures of Hematite for Visible-Light Photocatalysis

Construction of heterojunction ZnFe2O4/ZnO/Ag by using ZnO and Ag nanoparticles to modify ZnFe2O4 and its photocatalytic properties under visible light

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Facile synthesis of hierarchical Ag 3 PO 4 /TiO 2 nanofiber heterostructures with highly enhanced visible light photocatalytic properties

Formation of α-Fe2O3/FeOOH nanostructures with various morphologies by a hydrothermal route and their photocatalytic properties

Nanostructured hematite photoelectrochemical electrodes prepared by the low temperature thermal oxidation of iron

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Hematite Nanorods with Tunable Porous Structure: Facile Hydrothermal-Calcination Route Synthesis, Optical and Photocatalytic Properties

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Tunable Synthesis of Hematite Structures with Nanoscale Subunits for the Heterogeneous Photo-Fenton Degradation of Azo Dyes

TiO 2 Fibers Supported β-FeOOH Nanostructures as Efficient Visible Light Photocatalyst and Room Temperature Sensor

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Preparation Of Fe3+-Doped Tio2 Nanoparticles And Their Photocatalytic Activities

Sol-Gel Hydrothermal Synthesis and Visible Light Photocatalytic Degradation Performance of Fe/N Codoped TiO2 Catalysts

Hydrothermal preparation of α-Fe2O3 nano-scale spheres and their photocatalytic property study

Tailoring CuO Nanostructures for Enhanced Photocatalytic Property.

Evaluation of Photocatalytic Activity and Electrochemical Properties of Hematite Nanoparticles

Hydrothermal synthesis of TiO2/Ti3C2 nanocomposites with enhanced photocatalytic activity

Preparation and Enhanced UV Visible Light Photoelectrocatalytic Activity of TiO2 Fe2O3/Cu Ternary Nanocomposites