Abstract:The present paper focuses on the heat transfer and contact pressure at the casting-die interface in squeeze casting process. Experiments were conducted and a "plate shape" was used to cast aluminum alloy A356 in H13 steel die. Based on the temperature measurements inside the die, the interfacial heat transfer coefficient (IHTC) at the metal-die interface was determined by applying an inverse approach. The pressure at the metal-die interface was measured by using Kistler pressure transducer. The acquired data were processed by a low pass filtering method based on Fast Fourier Transform (FFT). Besides, a set of methods was set up to verify the computer program for the inverse model. The results show that the pressure at the casting-die interface and the IHTC rose to the peak value almost simultaneously as soon as the pressure was applied by the press. The higher the applied pressure, the higher the peak value of the IHTC and the pressure at the casting-die interface. It was a pressure maintaining stage immediately after the pressure was applied. During this stage, the pressure at the casting-die interface decreased immediately after it reached the peak value. The IHTC sharply dropped at the beginning. Then, the decrease rate of the IHTC became lower and lower. Besides, the IHTC of the cases with pressure applied was much higher than those without pressure applied. It indicates that the applied pressure greatly improved the contact status of casting and die surfaces and reduced the thermal resistance between the two surfaces. The IHTC profiles of the cases with the pressures 23 MPa and 46 MPa applied did not make much difference, however, when the applied pressure reached 70 MPa, the influence of the pressure at the casting die interface on the IHTC became very remarkable. (C) 2017 Elsevier Ltd. All rights reserved.

Pressurization Control System for Low Pressure Crucible Casting

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Quality Control Study on High Pressure Casting Based on Magma and Ultra-red Simulation

Low Pressure Sand Mould Casting Technology for Heavy Aluminum Alloy Casting

Optimization of the Synchronous Pressurization Process for the Elimination of Double-Layer Oxide Film Defects

Mold Local Temperature Control in Low Pressure Die Casting Aluminum Alloy Wheel Hub

Key Analysis of Design and Numerical Simulation for Aluminum Alloy Impeller Low-pressure Casting Mold

Finite element analysis for die casting parameters in high-pressure die casting process

Solidification simulation of automobile wheel in low pressure casting

Mechanism and Application of A Newly Developed Pressure Casting Process: Horizontal Squeeze Casting

Production of ZL205A Alloy Shell Castings by Low Pressure Casting

Reduction of Shrinkage Porosities in Aluminum Alloy Castings by External Pressure Fluctuation under Gravity Field

Preparation and Properties of Special Vehicle Cover Via a Novel Squeeze Casting Quantitative Feeding System of Molten Metal

Application of PLC on Pneumatic Control System for Differential-gravity Casting Equipment

Development of New Multi-Function System for Testing Linear Shrinkage and Stress and Hot Cracking of Casting Alloy

Adaptive Control of Nozzle Melt Packing Pressure

Low-pressure die casting of magnesium alloy AM50: Response to process parameters

Integrated optimization system for high pressure die casting processes

Research and Development of Cold Crucible Melting and Casting Technology

Experimental Study on the Heat Transfer Behavior and Contact Pressure at the Casting-Mold Interface in Squeeze Casting of Aluminum Alloy

Low pressure casting technology and forming process analysis of metal mold based on ProCAST FEA procedure