Abstract:Ni2P/SiO2, MoP/SiO2, and NiMoP/SiO2 with different Ni/Mo molar ratios were prepared by temperature-programmed reduction (TPR). Their structural properties were characterized by N-2, sorption, X-ray diffraction (XRD), CO chemisorption, X-ray photoelectron spectroscopy (XPS), H-2 temperature-programmed desorption (H-2-TPD), and NH3 temperature-programmed desorption (NH3-TPD). Their performances for the hydrodeoxygenation (HDO) of anisole were tested in a fixed-bed reactor. It was found that there were mainly three reactions that occurred during the HDO, i.e., the demethylation of anisole, the hydrogenolysis of phenol, and the hydrogenation of benzene. The HDO activities decreased in the sequence of Ni2P/SiO2 > NiMoP/SiO2 > MoP/SiO2. The NiMoP/SiO2 catalysts with larger Ni/Mo ratios had higher activities. In the phosphides, the Ni delta+ and Mo delta+ sites bearing small positive charges acted not only as Lewis acid sites for the demethylation but also as metal sites for the hydrogenolysis and hydrogenation. The Ni delta+ site was more active than the Mo delta+ site, and there was no synergy between the Ni delta+ and Mo delta+ sites. The superior activity of Ni2P to that of MoP is attributed to the higher d electron density in Ni2P. PO H groups, which acted as Bronsted sites and provided active hydrogen species, had less activity for the three reactions compared to the metal sites. In comparison to a conventional NiMo/gamma-Al2O3 catalyst, the Ni phosphide-containing catalysts had much higher activities. The catalyst deactivation due to water was preliminarily discussed. The oxidation of phosphide by water might lead to the formation of metal oxide and/or phosphate, leading to the catalyst deactivation. The high stability of Ni2P/SiO2 may be related to the ligand effect of P that lowers the electron density of Ni and inhibits the Ni-O combination.

Ni/Al2O3 Catalysts Derived from Layered Double Hydroxide and Their Applications in Hydrodeoxygenation of Anisole

NiMoAl Catalysts Derived from Heptamolybdate-Intercalated Layered Double Hydroxides for Hydrodeoxygenation of Anisole

Catalytic Hydrodeoxygenation of Anisole As Lignin Model Compound over Supported Nickel Catalysts

Hydrodeoxygenation of Anisole over Ni/α-Al2O3 Catalyst

An efficient bifunctional Ni-Nb2O5 nanocatalysts for the hydrodeoxygenation of anisole

Bimetallic Niobium-Based Catalysts Supported on SBA-15 for Hydrodeoxygenation of Anisole

Enhanced Hydrodeoxygenation of Lignin-Derived Phenolic Compounds by Regulating Support Composition of Ni/Al2O3-C Catalyst

Enhanced Hydrodeoxygenation of Lignin-Derived Anisole to Arenes Catalyzed by Mn-doped Cu/Al2O3

Hydrodeoxygenation of lignin-derived phenolics to cycloalkanes over Ni-Co alloy coupled with oxophilic NbOx

Hierarchical Mesoporous ZSM-5 Supported Nickel Catalyst for the Catalytic Hydrodeoxygenation of Anisole to Cyclohexane

Metallic nickel supported on mesoporous silica as catalyst for hydrodeoxygenation: effect of pore size and structure

Hydrodeoxygenation of Anisole over Silica-Supported Ni2P, MoP, and NiMoP Catalysts

Investigations into the influence of nickel loading on MoO 3 -modified catalysts for the gas-phase hydrodeoxygenation of anisole

Synergistic effect of acidity and active phases for nickel nanoparticles supported HZSM-5 catalysts on lignin-related model compounds hydrodeoxygenation performance under mild conditions

Hydrodeoxygenation of Lignin Model Compounds to Alkanes over Pd–Ni/HZSM-5 Catalysts

Hydrodeoxygenation of anisole over SBA-15-supported Ni, Pd, and Pt mono- and bimetallic catalysts: effect of the metal's nature on catalytic activity and selectivity

Selective hydrodeoxygenation of lignin-derived phenolics to cycloalkanes over highly stable NiAl<sub>2</sub>O<sub>4</sub> spinel-supported bifunctional catalysts

Effect of Zn on Performance of Ni/SiO2 for Hydrodeoxygenation of Anisole

Study on hydrodeoxygenation mechanism of anisole over Ni (111) by first-principles calculation

Hydrodeoxygenation Performance of Lignin-Derived Phenolics to Cycloalkanes: Insights into the Crystal Structures of the Nb2O5 Support