Abstract:This work reports on the syntheses of one-dimensional (1D) H2Ti3O7 materials (nanotubes, nanowires and their mixtures) by autoclaving anatase titania (Raw-TiO2) in NaOH-containing ethanol-water solutions, followed by washing with acid solution. The synthesized nanosized materials were characterized using XRD, TEM/HRTEM, BET and TG techniques. The autoclaving temperature (120-180 degrees C) and ethanol-to-water ratio (V(EtOH)/V(H2O) = 0/60 approximately 30/30) were shown to be critical to the morphology of H2Ti3O7 product. The obtained H2Ti3O7 nanostructures were calcined at 400-900 degrees C to prepare 1D-TiO2 nanomaterials. H2Ti3O7 nanotubes were converted to anatase nanorods while H2Ti3O7 nanowires to TiO2(B) nanowires after the calcination at 400 degrees C. The calcination at higher temperatures led to gradual decomposition of the wires to rods and phase transformation from TiO2(B) to anatase then to rutile. Photocatalytic degradation of methyl orange was conducted to compare the photocatalytic activity of these 1D materials. These 1D materials were used as new support to prepare Au/TiO2 catalysts for CO oxidation at 0 degrees C and 1,3-butadiene hydrogenation at 120 degrees C. For the CO oxidation reaction, Au particles supported on anatase nanorods derived from the H2Ti3O7 nanotubes (Au/W-180-400) were 1.6 times active that in Au/P25-TiO2, 4 times that in Au/Raw-TiO2, and 8 times that on TiO2(B) nanowires derived from the H2Ti3O7 nanotubes (Au/M-180-400). For the hydrogenation of 1,3-butadiene, however, the activity of Au particles in Au/M-180-400 was 3 times higher than those in Au/W-180-400 but similar to those in Au/P25-TiO2. These results demonstrate that the potential of 1D-TiO2 nanomaterials in catalysis is versatile.

Effect of Microstructures on the Acidity and Catalytic Performance for H2Ti3O7Nanomaterials

Promotional effect of Ti doping on the ketonization of acetic acid over a CeO2 catalyst

Tuning the Photoelectronic and Photocatalytic Properties of Single-Crystalline TiO 2 Nanosheet Array Films with Dominant {001} Facets by Controlling the Hydrochloric Acid Concentration

Effects of Acid on the Microstructures and Properties of Three-Dimensional TiO 2 Hierarchical Structures by Solvothermal Method

Structures and Brønsted Acidity Features for Titanoniobates with Different Laminate Composition

One-dimensional TiO2 nanomaterials: preparation and catalytic applications.

Mn−Co Mixed Oxide Nanosheets Vertically Anchored on H2Ti3O7 Nanowires: Full Exposure of Active Components Results in Significantly Enhanced Catalytic Performance

Enhanced Esterification Performance of Layered SO42−/TiO2‐H3Ti5NbO14 Solid Acid Catalyst

Surface Modification on Pd-TiO2 Hybrid Nanostructures Towards Highly Efficient H2 Production from Catalytic Formic Acid Decomposition.

High Catalytic Performance and Stability of Pt/C Using Acetic Acid Functionalized Carbon

Effect of Ph Value on H2Ti2O5/TiO2 Composite Nanotubes As Pt Catalyst Support for Methanol Oxidation

The Influence of the Crystal Structure of TiO2 Support Material on Pd Catalysts for Formic Acid Electrooxidation

Design of Pd{111}-TiO 2 Interface for Enhanced Catalytic Efficiency Towards Formic Acid Decomposition

Effect of Ph Value on the Microstructure and Deno(X), Catalytic Performance of Titanate Nanotubes Loaded Ceo2

Sulfated TiO2 Nanosheets Catalyzing Conversion of Biomass Derivatives: Influences of the Sulfation on Distribution of Brønsted and Lewis Acidic Sites

Preparation and Characterization of SO;/TiO; and S;O;/TiO; Catalysts

Effect of TiO2 crystal phase on the catalytic transfer hydrogenation using formic acid over the Pd/TiO2 catalyst

Preparation of TiO2-Nanorods Supported Pd Catalyst and Its Electrocatalytic Oxidation on Formic Acid

Nitric Acid-Pretreated Natural Halloysite Nanotubes As Ni Nanoparticle Catalyst Supports for CO2 Methanation

Study on the Co-Catalytic Effect of Titanium Dioxide and Titanate Nanomaterials on Platinum-Based Catalysts in Direct Alcohol Fuel Cells

Catalytic Performance Comparison of Shape-Dependent Nanocrystals and Oriented Ultrathin Films of Pt4Cu Alloy in the Formic Acid Oxidation Process