Preparation and Characterization of SO;/TiO; and S;O;/TiO; Catalysts

ma xuedan,guo daishi,jiang qizhong,ma zifeng,ma zhengfei,ye weidong,li chunbo
2006-01-01
Abstract:Nano-sized solid superacids SO42?/TiO2 and S2O82?/TiO2, as well as MCM-41 supported SO42?/ZrO2 were prepared. Their structures, acidities were investigated and compared through characterization methods of XRD, N2 adsorption-desorption, and in situ pyridine adsorption FTIR, and catalytic activities were evaluated by the cyclization reaction of pseudoionone cyclization. The results show that SO42?/TiO2 and S2O82?/TiO2 particles possess not only nanosize with diameters less than 7.0 nm, large BET surface larger than 140 cm2?g?1, and relatively regular mesostructures with pores size about 4.0 nm, but also pure anatase phase and strong acidity. Different from the Lewis acidity nature of SO42?/ZrO2/MCM-41, SO42?/TiO2 and S2O82?/TiO2 behave mainly Br?nsted acidities. The strongest Br?nsted acid sites are formed on SO42?/TiO2 promoted with H2SO4, while Lewis acid sites on S2O82?/TiO2 are even stronger than those on SO42?/ZrO2/MCM-41, and the former which are generated when persulfate solution is used as sulfating agent. The catalytic activities of SO42?/TiO2 and S2O82?/TiO2 for cyclization of pseudoionone are much higher than that of SO42?/ZrO2/MCM-41 due to their distinct acid natures, and it can be concluded that existence of more Br?nsted acid sites is favorable for the proton participating cyclization reaction.
What problem does this paper attempt to address?