Modulating crystal phase of Zr-based solid acid catalyst to boost synthesis of 9, 9-bis(4-hydroxyphenyl) fluorene
Jingjie Li,Lin Wang,Yanfeng Pu,Yong Liu,Xiying Li,Renren Sun,Yahui Xiao
DOI: https://doi.org/10.1039/d4re00457d
IF: 5.2002
2024-11-29
Reaction Chemistry & Engineering
Abstract:The crystal phase of Zr-based solid acid catalyst was modulated by two-step precipitation method for strongly bonding with sulfate groups. The catalytic performance of these catalysts was subsequently evaluated for condensation of 9-fluorenone with phenol. The results revealed that the catalytic activity of the catalysts was positively correlated with the acidity of the catalysts. Specifically, the SZr@Zr-2 catalyst exhibited the best catalytic performance with a 9-fluorenone conversion of 99.92% and 9,9-bis(4-hydroxyphenyl) fluorene (BHPF) selectivity of 99.86% under the optimized reaction condition of 110 °C, 3 h and phenol to 9-fluorenone mole ratio of 6. It was demonstrated that the Zr(OH)4@Zr(OH)4-2 substrate prepared by two-step precipitation inherited rich Zr(OH)4 species, which could be easily bonded with more sulfate groups. After calcination, these species were subsequently transformed into tetragonal ZrO2 species induced by sufficient interaction with sulfate groups. The coordination between sulfate groups and tetragonal ZrO2 enhanced the acidity of the SZr@Zr-2 catalyst and then boosted the condensation of 9-fluorenone with phenol for BHPF synthesis.
chemistry, multidisciplinary,engineering, chemical