Abstract:Provided a method to synthesize Nylon-6 oligomers with certain molecular weight and to further synthesize polyesteramides having short Nylon-6 segments connected by ester linkages. Polyamide prepolymer (PrePA) with molecular weight of 524. 6 to 808. 1 was synthesized by a ring-opening polymerization of epsilon-caprolactam in the presence of aminoethanol under the catalysis of H3PO3. The chain extension of the PrePAs was studied using N, N'-carbonylbiscaprolactamat (CBC) and 2, 2'-(1, 4-phenylene)-bis (2-oxazoline) (PBOX) as combined chain extenders. Through polycondensation of PrePA with adipic acid, polyesteramide prepolymers(PrePEA) with intrinsic viscosity of 0. 22 similar to 0. 30 dL/g were synthesized. Chain extension of the PrePEAs was carried out using PBOX and CBC as combined chain extenders and the chain extended polyesteramide (ExtPEA) with intrinsic viscosity up to 0. 74 dL/g was obtained. The ExtPEAs were characterized by FTIR and H-1-NMR spectra, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), wide angle X-ray scattering (WAXS) and tensile test. The DSC study showed that after chain extension the T-m and Delta H-m of the polyesteramides decreased. ExtPEA with [eta] of 0. 72 dL/g had the T-g of 30 degrees C and T-m of 163 degrees C. WAXS characterization showed that the ExtPEA had similar crystal characteristics to the Nylon-6 crystallites. TGA study showed that the ExtPEA had good thermal stability with initial decomposition temperature over 330 degrees C. Tensile test showed that typical ExtPEA samples had a tensile strength of 14. 1 MPa and a strain at break of 68. 6%. The ExtPEA has high Tm, good thermal stability and moderate tensile strength, and is suitable for melt processing. Meanwhile, presence of the ester linkages and lower crystallinity in the ExtPEA may lead to improved biodegradability of the ExtPEA compared to the normal nylon-6.

Segmented Poly(L-lactic acid)-Co-polyamides Synthesized through Polycondensation and Chain Extension

Poly(L-Lactic Acid)-Block-Poly(Butylene Succinate-Co-Butylene Adipate) Multiblock Copolymers: from Synthesis to Thermo-Mechanical Properties

Nucleating Agent-Containing P(Lla-Mb-Bsa) Multi-Block Copolymers with Balanced Mechanical Properties

Poly(L-Lactide) Materials with Balanced Mechanical Properties Prepared by Blending with Peg-Mb-Ppa Multiblock Copolymers

Amphiphilic Block Copolymers Based on Methoxy Poly(ethylene Glycol) and Either Crystalline or Amorphous Poly(caprolactone‐b‐lactide): Synthesis, Solid‐state and Aqueous Solution Characterizations

Enhanced Crystallization Rate and Mechanical Properties of Poly(l‐lactic Acid) by Stereocomplexation with Four‐armed Poly(ϵ‐caprolactone)‐block‐poly(d‐lactic Acid) Diblock Copolymer

Melt synthesis and characterization of poly(L-lactic acid) chain linked by multifunctional epoxy compound

Chain Extension of Adipic Acid and (or) Succinic Acid/butanediol Polyesters with 2,2′‐(1,4‐phenylene)‐bis(2‐oxazoline) and Adipoylbiscaprolactamate Combined Chain Extenders

Synthesis and Properties of Polyesteramides Having Short Nylon-610 Segments in the Main Chains Through Polycondensation and Chain Extension

Synthesis of Tri-arm PLLA-PDLA Block Copolymers and Its Stereocomplex Crystallization Behavior

Synthesis, Structures and Characterization of Triarm Ppo-Pdla-Plla Block Copolymers and Its Stereocomplex Crystallization Behavior

Chain Extension of Polybutylene Adipate and Polybutylene Succinate with Adipoyl‐ and Terephthaloyl‐biscaprolactamate

Catalyzed Chain Extension of Poly(butylene Adipate) and Poly(butylene Succinate) with 2,2′‐(1,4‐Phenylene)‐bis(2‐oxazoline)

Synthesis and characterization of polyesteramides having short Nylon-6 segments in the main chains through polycondensation and chain extension

Polymorphic Crystallization Behavior of a Poly(butylene adipate) Midblock within a Poly(L-lactide-butylene adipate-L-lactide) Triblock Copolymer

SYNTHESIS AND CHARACTERIZATION OF POLYESTERAMIDES DERIVED FROM Ε-Caprolactam AND AMINOETHANOL

Poly(L‐lactide)‐b‐poly(ε‐caprolactone)‐b‐poly(D,L‐lactide) copolymers with enhanced toughness and strength by regulating crystallization and phase separation

Polylactide-b-poly(ethylene-co-butylene)-b-polylactide thermoplastic elastomers: role of polylactide crystallization and stereocomplexation on microphase separation, mechanical and shape memory properties

Study on Biodegradable Polymer Materials Based on Poly(lactic Acid). I. Chain Extending of Low Molecular Weight Poly(lactic Acid) with Methylenediphenyl Diisocyanate

Enhancement of the properties of biodegradable poly(L-lactide)/poly(butylene carbonate) blends by introducing stereocomplex polylactide crystals

Tailoring the LCST of PNIPAAM-b-PLA-b-PNIPAAM triblock copolymers via stereocomplexation