Formation of a Nano-Pattering NiTi Surface with Ni-depleted Superficial Layer to Promote Corrosion Resistance and Endothelial Cell-Material Interaction

Tingting Zhao,Yan Li,Yun Xia,Subbu S. Venkatraman,Yan Xiang,Xinqing Zhao

DOI: https://doi.org/10.1007/s10856-012-4777-1

2013-01-01

Abstract:Zirconium ion implantation was performed on NiTi alloy to suppress Ni ion release as well as to improve corrosion resistance and cell-material interaction. A thicker Ni-depleted nano-scale composite layer formed after Zr implantation and the corrosion resistance was evidently increased in aspects of increased E (br) - E (corr) (difference between corrosion potential and breakdown potential) and decreased corrosion current density. 2.5/2 NiTi sample possessed the highest E (br) - E (corr), more than 500 mV higher than that of untreated NiTi, suggesting a significant improvement on pitting corrosion resistance. Ni ion release rate of Zr-NiTi was decreased due to the depletion of Ni in the superficial surface layer and the diffusion resistance effect of the ZrO2/TiO2 nano-film. Increased surface wettability induced by increased surface roughness was obtained after Zr implantation. Zr-NiTi samples were found to be favorable to endothelial cells (ECs) proliferation, especially after 5 and 7 days culture.