Abstract:The impact of Zn on the mechanical properties and corrosion resistance of Al-Mg-Si alloys with high Cu contents was studied through microstructure analysis and accelerated corrosion testing. The age-hardening response of the alloy improved with the addition of trace Zn, and the poor corrosion resistance caused by high Cu content was overcome. Intergranular corrosion susceptibility (IGC) decreased and then increased with increasing Zn content. Al-Mg-Si-Cu alloys that contain 0.5 wt.% Zn possessed the best corrosion resistance. Zn decreased the potential difference between the matrix and the Al(Mn, Fe)Si phases according to scanning Kelvin probe force microscopy (SKPFM) tests, which reduced the driving force of corrosion in the alloy. Additionally, the addition of Zn promoted discontinuous precipitation at the grain boundaries, which was conducive to enhancing the IGC resistance. However, excessive Zn (1.0 wt.%) promoted the diffusion of more solute atoms near the grain boundaries to the grain boundaries, which coarsened the precipitated phase at the grain boundaries and shortened the interphase distance. Moreover, as the width of the PFZ increased, the concentration of solute atoms decreased, and the potential difference between the precipitated phase and the PFZ increased, leading to more severe IGC behavior. Therefore, an appropriate Zn content was beneficial for improving the corrosion properties and age-hardening response of Al-Mg-Si-Cu alloys.

Combined Effect of Ag and Mg Additions on Localized Corrosion Behavior of Al-Cu Alloys with High Cu Content

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Influence of β-Mg 17 Al 12 and Al-Mn intermetallic compounds on the corrosion behaviour of cast and solution treated Mg-Al-Zn-Mn alloys

Effect of Ag on cathodic activation and corrosion behaviour of Mg-Mn-Ag alloys

Initial localized corrosion induced by multiscale precipitates in the new generation high-strength Al-Zn-Mg-Cu alloy

Effects of micro-alloying Ag on microstructure, mechanical properties and corrosion behavior of extruded Mg-2Zn-0.2Ca-xAg alloys

Effect of Al Addition and Heat Treatment on the Microstructures and Corrosion Resistance of Mg-Cu Alloys

Effect of Alloying Mg on Corrosion Resistance of Cu at High Temperature

In-situ AFM and quasi-in-situ studies for localized corrosion in Mg-9Al-1Fe-(Gd) alloys under 3.5 wt.% NaCl environment

Corrosion behavior characterization of as extruded Mg-8Li-3Al alloy with minor alloying elements (Gd, Sn and Cu) by scanning Kelvin probe force microscopy

Effects of Al addition on corrosion behavior and mechanical property of high-strength and high-elasticity Cu-20Ni-20Mn-0.3Nb-0.3Cr-0.3Zr alloy

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Unveiling the effect of Al-Mn intermetallic on the micro-galvanic corrosion of AM50 Mg alloy in NaCl solution

Effect of Trace Zn on the Mechanical Properties and Corrosion Behavior of Al-Mg-Si Alloys with High Cu

Microstructure, Mechanical Properties, and Corrosion Behavior of Al-4.0Cu-1.1Li-0.5Mg-xAg Alloys

Investigation on the microstructural evolution and corrosion behaviors of Zn-microalloyed Al-Cu-Li alloys

Effect of Ag addition on the microstructure and corrosion properties of Sn–9Zn lead-free solder

Comparative, Real-Time in Situ Monitoring of Galvanic Corrosion in Mg-Mg2Ca and Mg-MgZn2 Couples in Hank's Solution

Effect of Al Element on the Microstructure and Properties of Cu-Ni-Fe-Mn Alloys

Effect of micro-alloying element La on corrosion behavior of Al-Mg-Si alloys

Localized corrosion at nm-scale hardening precipitates in Al-Cu-Li alloys