Abstract:Nanocrystal substitutional semiconductor alloys Mg-3(BixSb1-x)(2) (nano-Mg-3(BixSb1-x)(2)) with a mean grain size of similar to 30 nm were prepared by mechanical alloying plus hot-pressing, and their dc electrical and thermoelectric properties were investigated from room temperature down to 20 K. The results indicated that lattice parameters a and c of nano-Mg-3(BixSb1-x)(2) increased linearly with increasing Bi content x, in agreement with Vegard's law. The dc resistivity rho of nano-Mg-3(BixSb1-x)(2) decreased monotonically with increasing x, and a drop of over five orders of magnitude was reached at 300K when x increased from 0 to 1. Moreover, the temperature behaviour of the resistivity of nano- Mg-3(BixSb1-x)(2) changed sensitively with x, and a transition from the semiconducting state (i.e. d rho/dT < 0) to the metallic state (d rho/dT > 0) occurred between x = 0.7 and 0.8. Meanwhile, this transition was verified by the measurements of the temperature behaviour of the Seebeck coefficient S of nano-Mg-3(Bi1-xSbx)(2) with different x. In addition, Mott's rho proportional to T-1/4 law was observed at lower temperature regimes for the nano-Mg-3(BixSb1-x)(2) ( x not equal 0), suggesting the occurrence of hopping conduction. Although experiments showed that the Seebeck coefficient of nano-Mg-3(Bi1-xSbx)(2) decreased monotonically with x, their thermoelectric power factors PF changed non-monotonically, and a maximum PF of 1.4 mu W cm(-1) K-2 was achieved at room temperature for x = similar to 0.8, which was more than three orders magnitude greater than that of monolithic Mg3Sb2.

Thermoelectric Performance of Mg2-Xcaxsi Compounds

Influence of Ca Substitution on the Thermoelectric Properties of Mg2Si

Preparation and Thermoelectric Properties of Mg2Si1−xSnx

Thermoelectric Performance of Sb-and La-Doped Mg 2 Si 0 . 5 Ge 0 . 5

Thermoelectric Properties of Quaternary Mg2Sn0.4Si0.6−xGex Alloys

Solid State Synthesis and Thermoelectric Properties of Mg-Si-Ge System

Thermoelectric Properties of N-Type La-doped Mg2Si Based Semiconductors

Multiscale Calculations of Thermoelectric Properties of N-Type Mg2si1-Xsnx Solid Solutions

Effect of Vacancies on the Thermoelectric Properties of Mg2Si1−xSbx(0⩽x⩽0.1)

High Figures Of Merit And Natural Nanostructures In Mg2si0.4sn0.6 Based Thermoelectric Materials

Thermoelectric Properties of Nanocrystalline (mg1−xznx)3sb2isostructural Solid Solutions Fabricated by Mechanical Alloying

Thermoelectric Properties Of N-Type Mg2si0.6-Ysbysn0.4 Compounds

Thermoelectric properties of n‐type Mg<sub>2</sub>Si<sub>0.6–<i>y</i></sub>Sb<i><sub>y</sub></i>Sn<sub>0.4</sub>compounds

Effects of Mg Substitution on the Thermoelectric Properties of Ca3Co4O9-Based Materials

Tunable microstructures and improved thermoelectric performance of Mg 2(Si0.4-xSbxSn0.6) solid solutions

Solid-State Synthesis of Mg2si1-Xyx(Y=Ge and Sn) Thermoelectric Materials Via Bulk Mechanical Alloying

Regulating thermoelectric properties of Eu0.5Ca0.5Zn2Sb2 through Mg dopant

Thermoelectric Properties of Zintl Compound Ca1−xNaxMg2Bi1.98

Effect of GaSb Addition on the Thermoelectric Properties of Mg2Si0.5Sn0.5 Solid Solutions

Thermoelectric Properties of Mg 2 (Si 0.3 Sn 0.7 ) 1− y Sb y Solid Solutions Doped with Co as CoSi Secondary Phase

Electrical And Thermoelectric Properties Of Nanocrystal Substitutional Semiconductor Alloys Mg-3(Bixsb1-X)(2) Prepared By Mechanical Alloying