Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Isothermal LCF fatigue behaviors of a single crystal nickel base superalloy at high temperatures

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

LCF behavior and lifing of a directionally solidified nickel base superalloy at high temperature

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

Research on Low Cycle Fatigue Damage and Macroscopic Anisotropic Constitutive Model of Ni-based Single Crystal Superalloy at Different Temperatures

A Low-Cycle Fatigue Life Model of Nickel-Based Single Crystal Superalloys under Multiaxial Stress State

High-temperature low cycle fatigue behavior of nickel based superalloy GH536

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Tensile and low cycle fatigue properties of nickel-base powder metallurgy superalloy FGH95

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

The Influence of Dwell Time on Low Cycle Fatigue Behavior of Ni-Base Superalloy Ic10

Low Cycle Fatigue and Creep-Fatigue Interaction Behavior of Nickel-Base Superalloy GH4169 at Elevated Temperature of 650 °C

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Cyclic Deformation Behavior of a Nickel-Base Superalloy under Fatigue Loading