Abstract:Zinc N,N′-piperazinebis(methylenephosphonic acid) (PPMPA-Zn) was melt blended with high-density polyethylene-g-maleic anhydride (HDPE-MA) to fabricate flame-retardant HDPE-MA/PPMPA-Zn composites. The thermal stability and flame retardancy of the composites were investigated by thermogravimetric analysis (TGA) and cone calorimetry. The incorporation of PPMPA-Zn did not appreciably increase the thermal stability of HDPE-MA, but the residual char content increased to 18.7% when the content of PPMPA-Zn reached 25 wt%. X-ray diffraction and Raman spectroscopy tests showed that the residual char was composed mainly of Zn(PO3)2, Zn11(HPO 3)8(OH)6 and amorphous graphite. Scanning electron microscopy (SEM) images of samples collected after cone calorimetric tests also confirmed the formation of char in the sample with 25 wt% PPMPA-Zn loading in HDPE-MA, and the char layer acted as a compact and intact physical barrier in the condensed phase. Even at a loading as low as 5 wt% PPMPA-Zn, the peak value of the heat release rate (PHRR) was reduced by 38% compared with that of pure HDPE-MA. In contrast to other intumescent flame retardants, the introduction of PPMPA-Zn enhanced not only the flame retardancy but also the mechanical properties of HDPE-MA. For example, the yield strength and Young's modulus of HDPE-MA with 5 wt% PPMPA-Zn were 125% and 128% higher, respectively, than those of the pure HDPE-MA matrix. © 2013 Elsevier B.V. All rights reserved.

Fabrication of Fullerene Decorated by Iron Compound and Its Effect on the Thermal Stability and Flammability for High‐density Polyethylene

Thermal Degradation and Flammability Properties of HDPE/EVA/C60 Nanocomposites

Thermal and thermo-oxidative degradation of high density polyethylene/fullerene composites

Improved Flame Retardant of Intumescent Flame Retardant Flame-Retarded High Density Polyethylene with Fullerene Decorated by Iron Compound

Fabrication of Fullerene-Decorated Graphene Oxide and Its Influence on Flame Retardancy of High Density Polyethylene

Improving The Flame-Retardant Efficiency Of Aluminum Hydroxide With Fullerene For High-Density Polyethylene

Kinetics and Mechanism of Thermal and Thermo-oxidative Degradation for High-density Polyethylene Modified by Fullerene and Its Derivative

Fabrication Of Fullerene-Decorated Carbon Nanotubes And Their Application In Flame-Retarding Polypropylene

Improving the flame retardancy and mechanical properties of high-density polyethylene-g-maleic anhydride with a novel organic metal phosphonate

Thermal Stability and Rheological Behaviors of High-Density Polyethylene/fullerene Nanocomposites

The Flame Retardant and Smoke Suppression Effect of Fullerene by Trapping Radicals in Decabromodiphenyl Oxide/sb2o3 Flame‐retarded High Density Polyethylene

Influence of fullerene on the kinetics of thermal and thermo-oxidative degradation of high-density polyethylene by capturing free radicals

Fabrication of 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-decorated Fullerene to Improve the Anti-Oxidative and Flame-Retardant Properties of Polypropylene

Effect of Friedel-Crafts Reaction on the Thermal Stability and Flammability of High-Density Polyethylene/brominated Polystyrene/graphene Nanoplatelet Composites

Decoration of layered double hydroxide-fullerene hybrid and its application for improving the thermal stability and antioxidant ability of high-density polyethylene

Fabrication of Fullerene Anchored Reduced Graphene Oxide Hybrids and Their Synergistic Reinforcement on the Flame Retardancy of Epoxy Resin

Thermal Stability and Oxygen Resistance of Polypropylene Composites with Fullerene/montmorillonite Hybrid Fillers

The effect of fullerene on the resistance to thermal degradation of polymers with different degradation processes

Influence of Fullerenes on the Thermal and Flame‐retardant Properties of Polymeric Materials

Effects of iron-based metal–organic framework-MIL-53(Fe) and phosphorus-based flame retardants on the flame retardancy of high-density polyethylene

Functionalized halloysite nanotubes endowing epoxy resin with simultaneously enhanced flame retardancy and mechanical properties