Abstract:The corrosion inhibition behaviors of dodecylpyridinium chloride (DPC), hexadecylpyridinium chloride monohydrate (HDPC), and the rosin amino acid surfactants dehydroabietic acylamino sodium (6-DAS) and compounds (6-DAS/DPC and 6-DAS/HDPC) were investigated by weight loss measurements and electrochemical testing. Besides, corrosion inhibition performance was further verified by combining a series of surface properties analyses and theoretical calculations. The weight loss results showed that the increase in inhibition efficiency was mainly attributed to its high concentration and revealed that the inhibition efficiency of compound inhibitors was higher than that of single inhibitor 6-DAS (92.23%), which was up to 95.86% and 96.72% of 6-DAS/DPC and 6-DAS/HDPC at 1:8 concentration ratio, respectively. The potential polarization curve potential demonstrated that single inhibitor 6-DAS and compound inhibitors (6-DAS/DPC and 6-DAS/HDPC) were both mixed-type corrosion inhibitors dominated by the anode. Thus, among the three, 6-DAS/HDPC had the best corrosion inhibition performance, and the average inhibition efficiency was 96.90%. Surface studies presented the adsorption of inhibitor molecules adhered on the Fe surface, while the adsorption performance of compound inhibitors appeared to be superior to single inhibitor 6-DAS. Moreover, it was found that there were a few excellent data from molecular dynamics simulation about the adsorption energies of inhibitors that could also explain the corrosion inhibitor performance, the results of which had good agreement with the experimental data, which provided strong evidence for the close relationship between the molecular structure of inhibitor and its inhibition efficiency.

Corrosion Inhibition of Q235 Steel by Ionic Liquid Based on the 2-(Dimethylamino) ethyl Methacrylate

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Corrosion Inhibition Of Q235 Steel By Octyl Dimethyl Benzyl Quaternary Ammonium Salt Ionic Liquid

A Dissymmetric Bis-Quaternary Ammonium Salt Gemini Surfactant As Effective Inhibitor for Q235 Steel in Hydrochloric Acid

Corrosion Inhibition of Dissymmetric Bis-Quaternary Ammonium with Imidazoline Ring on Q235 Steel in 1.0 Mol•l<sup>-1&Lt;/sup> Hydrochloric Acid Solution

Corrosion Inhibition of Dissymmetric Bis-Quaternary Ammonium with Imidazoline Ring on Q235 Steel in 1.0 mol•L<sup>-1</sup> Hydrochloric Acid Solution

Inhibition Performance of Novel Dissymmetric Bisquaternary Ammonium Salt to Q235 Steel in Hydrochloric Acid

Corrosion Inhibition Mechanism of Imidazoline-Based Dissymmetric Bis-Quaternary Ammonium Salts with Different Hydrophobic Chain Length on Q235 Steel in 1 M HCl Solution

Single and Double Alkyl Chain Quaternary Ammonium Salts as Environment-Friendly Corrosion Inhibitors for a Q235 Steel in 0.5 mol/L H2SO4 Solution

Halogen-Free Functional Quaternary Ammonium-Based Ionic Liquid As an Ecofriendly Corrosion Inhibitor for Q235 Steel in Acids.

Adsorption Activity and Molecular Dynamics Study on Anti-corrosion Mechanism of Q235 Steel

Corrosion Inhibition of PEG-TA Amphiphilic Block Copolymer on Q235 Steel in 1 mol/L HCl Medium

The inhibition performance of heterocyclic compounds on Q235 steel in methanol/formic acid medium: Experimental and theory

Effect of imidazoline derivatives on the corrosion inhibition of Q235 steel in HCl medium: experimental and theoretical investigation

The inhibitor effect of migrating corrosion inhibitors on Q235 steel in high alkaline environment under cathodic polarization

Adsorption and Corrosion Inhibition Properties of Pyridine‐2‐aldehyde‐2‐quinolylhydrazone for Q235 Steel in Acid Medium: Electrochemical, Thermodynamic, and Surface Studies

Inhibition Performance of Novel Dissymmetric Bisquaternary Ammonium Salt with an Imidazoline Ring and an Ester Group

Investigation of a Hydrophobically Associating AMAHS Polyacrylamides: A New Corrosion Inhibitor for Mild Steel in HCl

Corrosion inhibition performance of synergistic inhibitors on Q235 steel in methanol/formic acid medium

Synthesis of Gemini-type imidazoline quaternary ammonium salt using by-product fatty acid as corrosion inhibitor for Q235 steel

Experimental and Theoretical Analysis of Quinoline Diquaternary Ammonium Salt as Corrosion Inhibitor