Abstract:Different vinyl acetate (VAc) and vinyl benzoate (VBz) monomer ratios have been chosen as monomers to create high polymerization degree (Pn) and high syndiotacticity‐diad content (S‐diad) poly(vinyl alcohol) (PVA) polymers via emulsifier‐free polymerization in order to address the problem of limited mechanical capabilities of PVA fibers prepared with low Pn and low S‐diad polymer. The variations in hydrogen bonding, Pn, S‐diad, and viscosity of different PVA polymers were investigated and evaluated using Fourier transform infrared spectroscopy, proton nuclear magnetic resonance, gel permeation chromatography, and a viscosity tester. Moreover, various PVA fibers with high strength and modulus have been manufactured using a synthetic polymer as the raw material for dry‐wet spinning. The effect of Pn and S‐diad on the mechanical and thermal characteristics of PVA fibers is evaluated using a variety of characterization techniques, such as the scanning electron microscope, differential scanning calorimetry, thermogravimetric analyzer, X‐ray diffraction, and tensile tester. As the ratio of VBz monomer increased, the results suggested that VBz may have a considerable impact on the Pn and S‐diad of PVA polymers, the OH vibration absorption peak reduced from 3491 to 3442 cm−1; the Pn increased from 2112 to 17,704; and the S‐diad rose from 51.2% to 60.1%. In addition to the fact that Pn and S‐diad significantly increased the fibers' strength and modulus, the crystallinity increased from 41.8% to 51.7%, and the orientation degree rose from 87.5% to 91.7%, as Pn and S‐diad increased; the tensile strength and highest elastic modulus increased from 9.71 ± 0.3 cN/dtex to 12.74 ± 0.5 cN/dtex (increased of 31.2%) and 264.52 ± 9.3 cN/dtex to 338.41 ± 8.6 cN/dtex (increased of 27.9%); the elongation at break decreased from 5.63 ± 0.3% to 2.92 ± 0.2%.

PVA Microcrystalline Cross-linking and SA/PAA Double Network Synergistic Modification of SA Fiber

Simultaneous Enhancement of Strength and Toughness of PLA Induced by Miscibility Variation with PVA.

Dual roles of sodium polyacrylate in alginate fiber wet-spinning: Modify the solution rheology and strengthen the fiber

Preparation of Calcium Alginate/polyethylene Glycol Acrylate Double Network Fiber with Excellent Properties by Dynamic Molding Method.

Improvement In Mechanical And Hygroscopic Properties Of Modified Sa Fiber Crosslinking With Pegde

Evaluation and correlation of electrochemical and mechanical properties of PVA/SA nanofibres

Electrochemical characterization of PVA/SA nanofibers obtained by electrospinning processing

Fabrication and performance of octyl-grafted amphiphilic alginate derivative/polyvinyl alcohol blend nanofibers by electrospinning method

Effect of the solid content of spinning solutions on the structure properties of large-diameter polyvinyl alcohol fiber

Covalently Cross-Linked Ultrastrong SiO2-loaded Polyvinyl Alcohol Fibers Via Microfluidic Spinning

Preparation and characterization of polyvinyl alcohol/sodium alginate/Pyrovatex CP composite fibers

Preparation and properties characterization of silk fibroin/sodium alginate composite fiber

Sodium Alginate-Polyethylene Glycol Diacrylate Based Double Network Fiber: Rheological Properties of Fiber Forming Solution with Semi-Interpenetrating Network Structure.

Cross-Striation Structure of High Strength and High Modulus PVA Fiber

Doping Nanocellulose Crystal with Poly(vinyl Alcohol) for Water-Resistant Composite Fibers with Enhanced Mechanical and Dyeing Performances

Design for Dynamic Hydrogen Bonding in a Double Network Structure to Improve the Mechanical Properties of Sodium Alginate Fibers

Structure and properties of Col/PVA composite fiber crosslinked with BTCA

Preparation and characterization of high strength and high modulus PVA-La fiber with synthesized syndiotacticity-rich high polymerization degree PVA polymers as raw materials

Preparation of high‐strength, high‐modulus PVA fiber by synthesis of syndiotacticity‐rich high molecular weight PVA polymers with VAc and VBz via emulsifier‐free emulsion polymerization

Cellulose Fibers Modified By Pva-Based Polymers Via Grafting And Adsorption

Effect of SA solution concentration on formation of SA/PCL nanofiber via emulsion electrospinning process