Structure and properties of Col/PVA composite fiber crosslinked with BTCA

Li Junfan,Wei Xiao,Xu Jianjun,Ye Guangdou,Jiang Mengjin
DOI: https://doi.org/10.3969/j.issn.1001-0041.2013.04.005
2013-01-01
Abstract:The blend spinning solution of collagen(Col) and polyvinyl alcohol(PVA) was added with 1,2,3,4-butanetetracarboxylic acid(BTCA) as a crosslinker and was wet spun into as-spun fiber which was exposed to heat drawing and setting and acetalization to prepare Col/PVA composite fiber.The structure and properties of Col/PVA composite fiber were analyzed.The results showed that BTCA can promote the formation of crosslinking structure and improve the stability of Col in the fiber interior.The IR analysis showed that ester bond formed as BTCA reacted with the hydroxyl group of PVA.The scanning electron microscopy observation showed that the interior of the composite fiber had fewer holes and defects and became denser after crosslinking with BTCA.The differential scanning calorimetry analysis showed that the crosslinking effect of BTCA could depress the crystallization of PVA and cause the crystallinity to decrease;the composite fiber had excellent comprehensive properties comprising the breaking strength,elongation at break,Col retention rate and water softening point of 4.94 cN/dtex,12.56%,91.09% and 106 ℃,respectively.
What problem does this paper attempt to address?