Effect of SA solution concentration on formation of SA/PCL nanofiber via emulsion electrospinning process

Junjie Lin,Weihong Xu,Lingli Deng,Yurong Yan

DOI: https://doi.org/10.3969/j.issn.1001-0041.2017.06.002

2017-01-01

Abstract:A composite nanofiber with the lipophilic and hydrophilic two-phase structure was prepared by emulsion electrospin-ning process.A water-in-oil ( W/O) emulsion was prepared by using polycaprolactone ( PCL)/trichloromethane as a continuous phase, sodium alginate (SA)/deionized water as the dispersed phase and sorbitan monoleate(Span80) as the emulsifier, which was produced into SA/PCL composite nanofiber membrane via emulsion electrospinning process and was replaced with Ca2+to produce calcium alginate( CA)/PCL composite fiber membrane.The effect of SA solution concentration on the fiber formation was studied.The result showed that the addition of surfactant Span80 and dispersed phase SA aqueous solution could efficiently im-prove the spinnability of PCL;the SA solution concentration did not have an obvious effect on the viscosity of SA/PCL emulsion when the volume of SA solution was specific in the emulsion system;the surface tension of SA/PCL emulsion was decreased and the diameter of SA/PCL composite nanofiber reached a maxima, but was lower than that of the PCL nanofiber merely added with Span80, when the concentration of SA solution was increased; and SA migrated to the fiber surface during the electrospinning process and Ca2+ion-substitute reaction occurred, thus an adhesive structure formed between fibers after ion exchange.