Abstract:High temperature proton exchange membrane fuel cells (HT-PEMFCs) can operate over 100 °C without humidification, which avoids the catalyst poisoning and enhances the efficiency of the power conversion. However, the classic phosphoric acid (PA) doped polybenzimidazole (PBI) still remains the challenge in the trade-off between mechanical strength and proton conductivity. The γ-(2,3-epoxypropoxy) propyltrimethoxysilane (KH560), as a crosslinking agent, is widely used to improve the mechanical properties of membranes. Although it can enhance the mechanical strength of PBI membranes, it sacrifices the hydrogen of imidazole groups, resulting in a decrease in proton conductivity. In this present work, silane-crosslinked PBI proton exchange membranes (PEMs) were synthesized by the reaction between the pyridine-bridged PBI containing different hydroxyl (-OH) content with KH560. Through comprehensive structural characterization of the polymer and model compound, it has been determined that this crosslinking method does not compromise the N–H acidic sites on the imidazole ring. The crosslinking agent KH560 provides additional hydroxyl groups to PBI and participates in the construction of hydrogen bonding networks after the ring-opening reaction. It was found that the addition of pyridine and hydroxyl groups could promote the phosphoric acid uptake, and the appropriate degree of silane crosslinking could maintain the PBI membranes with reasonable mechanical properties. Proton conductivity and HT-PEMFCs performance of the obtained crosslinked films were further enhanced with the dimensional stability, thermal stability and mechanical properties. Among them, CPyOPBI–OH–20 presented the best overall performance, exhibiting the highest proton conductivity of 0.095 S cm−1 and the maximum power density of 767 mW cm−2 at 180 °C under the anhydrous condition, which was 4.2 times that of OPBI (182 mW cm−2).

Siloxane Crosslinked Imidazolium PPO/PTFE Membranes for High Temperature Proton Exchange Membranes

Novel Cross-Linked Membranes Based on Polybenzimidazole and Polymeric Ionic Liquid with Improved Proton Conductivity for HT-PEMFC Applications

Polybenzimidazole/ionic-liquid-functional Silica Composite Membranes with Improved Proton Conductivity for High Temperature Proton Exchange Membrane Fuel Cells

Cross-Linkable Polymeric Ionic Liquid Improve Phosphoric Acid Retention and Long-Term Conductivity Stability in Polybenzimidazole Based PEMs

Composite Membranes Based on Polybenzimidazole and Ionic Liquid Functional Si–O–Si Network for HT-PEMFC Applications

Phosphoric acid doped imidazolium silane crosslinked poly(epichlorihydrin)/PTFE as high temperature proton exchange membranes

Fabrication and investigation of phosphoric acid doped imidazolium siloxane crosslinked poly(2,6‐dimethyl‐1,4‐phenylen oxide) for high temperature polymer electrolyte membranes

Strengthening Phosphoric Acid Doped Polybenzimidazole Membranes with Siloxane Networks for Using As High Temperature Proton Exchange Membranes

Formation and investigation of dual cross-linked high temperature proton exchange membranes based on vinylimidazolium-functionalized poly(2,6-dimethyl-1,4-phenylene oxide) and polystyrene

Quaternized Poly(aromatic Ether Sulfone) with Siloxane Crosslinking Networks As High Temperature Proton Exchange Membranes

A novel poly(2,6-dimethyl-1,4-phenylene oxide) with pendant imidazolium groups for high-temperature proton exchange membrane

Preparation and investigation of high-temperature proton exchange membranes based on phosphoric acid doped imidazolium polysilsesquioxane crosslinked poly(vinyl chloride)

Crosslinked Polybenzimidazoles Containing Functional CrosslinkersAs High-Temperature Proton Exchange Membranes: Enhanced Strength and Conductivity

Introduction of polymeric ionic liquids containing quaternary ammonium groups to construct high-temperature proton exchange membranes with high proton conductivity and stability

Construction of High-Performance, High-Temperature Proton Exchange Membranes through Incorporating SiO2 Nanoparticles into Novel Cross-linked Polybenzimidazole Networks

Epoxides Cross-Linked Hexafluoropropylidene Polybenzimidazole Membranes for Application As High Temperature Proton Exchange Membranes

Cyano crosslinked polybenzimidazole membranes containing 4,5-diazafluorene and pyridine for high temperature proton exchange membranes

Novel cross-linked membranes based on polybenzoxazine and polybenzimidazole containing 4-phenyl phthalazinone moiety for high-temperature proton exchange membrane

Silane-crosslinked polybenzimidazole with different hydroxyl content for high-temperature proton exchange membrane

Preparation and Properties of Proton Exchange Membranes Based on Heteropolyacids Doped Polyacrylonitrile/Silica Composites

Sulfonated Polyphosphazene-Blended Self-Cross-Linked Polybenzimidazole-Based High-Temperature Proton Exchange Membranes: High Efficiency in Proton Transport at Low Humidity