Preparation And Properties Characterization Of Biobased Dihydrocoumarin Toughened Epoxy Resin

Han Tao,Cai Xiaoxia,Li Cong,Qiao Congde,Zhao Hui

DOI: https://doi.org/10.7503/cjcu20190007

2019-01-01

Abstract:A kind of 3D polymeric network, obtained through alternating copolymerization of dihydrocoumarin (DHC) and epoxides with the aid of chromium (III) complexes and bis ( triphenylphosp-hosphoranylidene ) ammonium chloride(PPNCl) catalysts, was introduced into the diglycidyl ether of bisphenol A (DGEBA) matrix to build a double network structure. This structure can achieve an effective stress transfer and energy absorption for the DGEBA toughness. The gel permeation chromatography (GPC) results showed that the molecular weight of DHC-net increased with the react time. DHC-based network (DHC-net) structure was confirmed via the H-1 NMR spectrum. Moreover, the chemical structures of epoxy resin (EP) , DHC-net and EP/DHC-net double networks were confirmed via the FTIR spectra. DMA, DSC and TGA tests indicated that a good compability between the DHC-based network and the DGEBA matrix. Mechanical test showed that an obvious increase in the elongation at break was achieved after the DHC-based network was introduced into the DGEBA matrix. Furthermore, compared to the neat DGEGA resin, remarkable improvements in tensile and impact strength were found after the introduction of DHC-based network with content no higher than 30% ( mass fraction) into the DGEBA matrix.