Favorable Interfacial Chemomechanics Enables Stable Cycling of High-Li-Content Li–In/Sn Anodes in Sulfide Electrolyte-Based Solid-State Batteries
Christian Hänsel,Baltej Singh,David Kiwic,Pieremanuele Canepa,Dipan Kundu,Christian Hänsel
DOI: https://doi.org/10.1021/acs.chemmater.1c01431
IF: 10.508
2021-07-29
Chemistry of Materials
Abstract:Solid-state batteries (SSBs) can offer a paradigm shift in battery safety and energy density. Yet, the promise hinges on the ability to integrate high-performance electrodes with state-of-the-art solid electrolytes. For example, lithium (Li) metal, the most energy-dense anode candidate suffers from severe interfacial chemomechanical issues that lead to cell failure. Li alloys of In/Sn are attractive alternatives, but their exploration has mostly been limited to the low capacity (low Li content) and In-rich LixIn (x ≤ 0.5) systems. Here, the fundamental electro-chemo-mechanical behavior of Li–In and Li–Sn alloys of varied Li stoichiometries is unraveled in sulfide electrolyte-based SSBs. The intermetallic electrodes developed through a controlled synthesis and fabrication technique display impressive (electro)chemical stability with Li6PS5Cl as the solid electrolyte and maintain nearly perfect interfacial contact during the electrochemical Li insertion/deinsertion under an optimal stack pressure. Their intriguing variation in the Li migration barrier with composition and its influence on the observed Li cycling overpotential is revealed through combined computational and electrochemical studies. Stable interfacial chemomechanics of the alloys allow long-term dendrite free Li cycling (>1000 h) at relatively high current densities (1 mA cm–2) and capacities (1 mAh cm–2), as demonstrated for Li13In3 and Li17Sn4, which are more desirable from a capacity and cost consideration compared to the low-Li-content analogues. The presented understanding can guide the development of high-capacity Li–In/Sn alloy anodes for SSBs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01431.Additional experimental details; diffraction pattern of the Li–In and Li–Sn alloys; SEM micrographs of the alloys and the fabricated electrodes; resistance of the SE pellets; stack resistance of A|Li6PS5Cl|A (A = Li, In, Li0.5In, LiIn, Li13In3 Li2Sn5, or Li17Sn4) cells; stripping and plating performance of metallic lithium and long-term stripping and plating performance of cells assembled with Li0.5In and LiIn; computational details; a list of the compound studied with modeling, their provenance, and the definition of the formation energy; and the additional Li migration barriers in selected alloys (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical