Abstract:Very often, pure Ti and (α + β) Ti-6Al-4V alloys have been used commercially for implant applications, but ensuring their chemical, mechanical, and biological biocompatibility is always a serious concern for sustaining the long-term efficacy of implants. Therefore, there has always been a great quest to explore new biomedical alloying systems that can offer substantial beneficial effects in tailoring a balance between the mechanical properties and biocompatibility of implantable medical devices. With a view to the mechanical performance, this study focused on designing a Ti-15Zr-2Ta-xSn (where x = 4, 6, 8) alloying system with high strength and low Young's modulus prepared by a powder metallurgy method. The experimental results showed that mechanical alloying, followed by spark plasma sintering, produced a fully consolidated (α + β) Ti-Zr-Ta-Sn-based alloy with a fine grain size and a relative density greater than 99%. Nevertheless, the shape, size, and distribution of α-phase precipitations were found to be sensitive to Sn contents. The addition of Sn also increased the α/β transus temperature of the alloy. For example, as the Sn content was increased from 4 wt.% to 8 wt.%, the β grains transformed into diverse morphological characteristics, namely, a thin-grain-boundary α phase (αGB), lamellar α colonies, and acicular αs precipitates and very low residual porosity during subsequent cooling after the spark plasma sintering procedure, which is consistent with the relative density results. Among the prepared alloys, Ti-15Zr-2Ta-8Sn exhibited the highest hardness (s340 HV), compressive yield strength (~1056 MPa), and maximum compressive strength (~1470). The formation of intriguing precipitate–matrix interfaces (α/β) acting as dislocation barriers is proposed to be the main reason for the high strength of the Ti-15Zr-2Ta-8Sn alloy. Finally, based on mechanical and structural properties, it is envisaged that our developed alloys will be promising for indwelling implant applications.

Additive Manufacturing of In-Situ Reinforced Ti–35Nb–5Ta–7Zr (TNTZ) Alloy by Selective Electron Beam Melting (SEBM)

Improved mechanical and wear properties of Ti−35Nb−5Ta−7Zr−xSi alloys fabricated by selective electron beam melting for biomedical application

Microstructural Evolution, Mechanical Properties, and Preosteoblast Cell Response of a Post-Processing-Treated TNT5Zr β Ti Alloy Manufactured via Selective Laser Melting

Low-modulus Biomedical Ti-30Nb-5Ta-3Zr Additively Manufactured by Selective Laser Melting and Its Biocompatibility.

Additively Manufactured Biomedical Ti-Nb-Ta-Zr Lattices with Tunable Young's Modulus: Mechanical Property, Biocompatibility, and Proteomics Analysis.

Effect of Silicon Content on the Microstructure Evolution, Mechanical Properties, and Biocompatibility of Β-Type TiNbZrTa Alloys Fabricated by Laser Powder Bed Fusion.

Additive Manufacturing of the High-Strength and Low Modulus Biomedical Ti-10 Nb Alloy under Reactive Atmosphere

Effect of Si addition on microstructure and performance of a biomedical Ti-Nb-Zr-Ta alloy prepared via powder hot extrusion

Increasing strength of a biomedical Ti-Nb-Ta-Zr alloy by alloying with Fe, Si and O

Alloy Design and Fabrication of Duplex Titanium-Based Alloys by Spark Plasma Sintering for Biomedical Implant Applications

High–Strength Porous TiNbZrTaFe Alloys Fabricated by Sintering of Nanocomposite Powder Precursor with Space Holder Technique

Microstructure Evolution and Superelasticity of Ti-24Nb-xZr Alloys Fabricated by Spark Plasma Sintering

Combined First-Principles and Experimental Study on the Microstructure and Mechanical Characteristics of the Multicomponent Additive-Manufactured Ti-35Nb-7Zr-5Ta Alloy

In vitro evaluation of the biocompatibility and bioactivity of a SLM-fabricated NiTi alloy with superior tensile property

Overcoming the Strength–ductility Trade-off by Tailoring Grain-Boundary Metastable Si-containing Phase in Β-Type Titanium Alloy

Microstructures and Mechanical Properties of a New Titanium Alloy for Surgical Implant Application

Microstructure and Corrosion Resistance of Powder Metallurgical Ti-Nb-Zr-Mg Alloys with Low Modulus for Biomedical Application

Microstructures and Wear Properties of Surface Treated Ti–36Nb–2Ta–3Zr–0.35O Alloy by Electron Beam Melting (EBM)

Synthesis and Characterization of a Novel Biocompatible Alloy, Ti-Nb-Zr-Ta-Sn

Mechanical Properties of Biomedical ß-Type Titanium Alloy with Rare-Earth Metal Oxide Particles Formed by Rare-Earth Metal Addition

Phase Selection-Oriented Mechanical Properties Tailoring for Β-Type TiNbZrTaSi Alloy Fabricated by Laser Powder Bed Fusion