Reduce Synthesis Temperature and Improve Dispersion of YAG Nanopowders Based on the Co-Crystallization Method

G. F. Fan,Y. Q. Tang,W. Z. Lu,X. R. Zhang,X. Xu

DOI: https://doi.org/10.1016/j.jallcom.2014.08.074

IF: 6.2

2014-01-01

Journal of Alloys and Compounds

Abstract:Pure yttrium aluminum garnet (YAG) nanopowders were synthesized at 950 degrees C from the co-crystallization precursor of Y(NO3)(3)-6H(2)O and Al(NO3)(3)center dot 9H(2)O (nitrate process). When 17 wt.% of Y(NO3)(3 center dot)6H(2)O was replaced by Y2O3 nanopowders, so as to make up a three-layer core-shell structure of the precursor, the synthesis temperature was reduced to 850 degrees C (Y2O3 process). Based on Y2O3 process, further reducing the synthesis temperature to 700 degrees C was realized by adding polyacrylic acid (PAA, 50% M), which was used to shorten the distance of the metal ions and provide combustion heat (PAA process). TEM characterizations indicated that the powders produced through nitrate and Y2O3 processes agglomerated, while the powders produced through PAA process were dispersed much better. The agglomerate size analysis results demonstrated that the powders produced through PAA process were with smaller agglomerate size and wider agglomerate size distribution than those through nitrate process or Y2O3 process. And they were more likely to be sintered to YAG transparent ceramics. (C) 2014 Elsevier B.V. All rights reserved.