Systematic optimization of spray drying for YAG transparent ceramics

le zhang,hao yang,xuebin qiao,tianyuan zhou,zhongying wang,jian zhang,dingyuan tang,deyuan shen,qitu zhang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2015.02.004
IF: 5.7
2015-01-01
Journal of the European Ceramic Society
Abstract:Spray drying parameters have been systematically optimized to granulate a stoichiometric mixture of commercial oxides for YAG transparent ceramics. The processing parameters and suspension composition were changed in sequence and SEM analysis, EDS, MIP and transmittance measurements, were used to choose the best spray drying parameters. The optimized inlet and outlet temperatures of drying medium were 75 and 60°C, and its flux and aspiration rate were 25Hz and 30Hz, respectively. The balanced suspension composition were: solid content 45wt.%, binder PVB 1.0wt.%, dispersant DS005 0.50wt.% and the atomizer rotating speed 8000r/min. The granulated particles exhibited excellent forming performance with mono-dispersed, spherical and fully dense aggregates, and mean size was ∼40μm. They could be crushed under 40MPa. The homogeneous distribution and microstructure of ceramics assured the high optical quality of YAG ceramics.
What problem does this paper attempt to address?