Densification and Microstructural Evolution of Yttria Transparent Ceramics: the Effect of Ball Milling Conditions

Jun Wang,Jian Zhang,Dewei Luo,Hao Yang,Dingyuan Tang,Ling Bing Kong

DOI: https://doi.org/10.1016/j.jeurceramsoc.2014.09.042

IF: 5.7

2015-01-01

Journal of the European Ceramic Society

Abstract:Ho:Y2O3 ceramics were prepared by using solid-state reaction method with commercial oxide powders. The effect of ball milling condition, specifically slurry concentration (CS), on densification, microstructure evolution and transmittance of the Ho:Y2O3 ceramics was studied. Ho:Y2O3 powders were ball milled with slurry concentrations of 33.2–17.4 vol%. The samples were vacuum sintered between 1400 and 1850°C. Over the CS range of 33.2–18.4 vol%, decreasing slurry concentration improved the densification, normal grain growth and optical transmittance of the Ho:Y2O3 ceramics. The 18.4 vol% Ho:Y2O3 powders showed the lowest agglomeration and highest densification rate, from which the ceramics prepared have the best transmittance. The grain growth exponents of the Ho:Y2O3 ceramics during final-stage of sintering were also studied.