Abstract:The study mainly investigates the effect of strain ratio on the multiaxial low cycle fatigue behaviour of 316L at 550 °C. The evolution of both axial and torsional stress amplitude is observed to go through three stages: cyclic hardening, softening and fracture. What's different is that the torsional loading experiences fewer cyclic hardening cycles compared to the axial loading. Regarding the interaction between axial and torsional stresses, it is observed that as the torsional strain increases, the axial deformation response presents a lower peak stress and a higher softening rate, while the torsional peak stress and softening rate hardly changes with the increase of axial strain amplitude. The fracture pattern is obtained through three-dimensional (3D) depth-of-field observation. It is discovered that as the strain ratio increases, the fracture pattern transits from tensile failure mode to shear failure mode. Furthermore, the orientation angle of the fracture surface increases and lies between the critical plane angle of maximum shear strain and maximum normal strain, indicating a mixed failure mode. Additionally, a comparison of nine representative critical plane models reveals that the energy-based models can better predict the multiaxial fatigue life influenced by the strain ratio. Finally, based on the analysis of deformation and failure mechanisms, a normal damage parameter weakening factor (NDWF) is introduced into the KBM-R model, and an improved normal stress component (INSC) is introduced into the Wu-R model. The two modified models well capture the impact of strain ratio and accurately predict the multiaxial fatigue life of both 316L and P92 steel.

Environmentally Assisted Fatigue Behavior of 308L Weld Metal in Borated and Lithiated High-Temperature Water

Recent progress in fatigue behavior of Mg alloys in air and aqueous media: A review

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Environment assisted cracking of 308L weld metal in high temperature water

Effect of thermal aging on the environmental assisted cracking behavior of 308L weld metal in high temperature water

Effects of strain rate on low-cycle fatigue crack growth behavior of 316LN weld metal in high-temperature pressurized water

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Low cycle fatigue behavior of 316LN stainless steel hollow specimen in air and liquid lead-bismuth eutectic

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Effect of surface roughness on low-cycle fatigue behaviors of 316LN stainless steel in borated and lithiated high-temperature pressurized water

Isothermal and thermomechanical fatigue behavior of 316LN stainless Steel: Effects of strain amplitude

Environment-Assisted Fatigue Crack Growth Along A1-6061/Epoxy Interface

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

Effects of Dwell Time on the Isothermal and Thermomechanical Fatigue Behavior of 316LN Stainless Steel

Fatigue Behavior of 316 L Stainless Steel Weldment Up to Very-High–cycle Fatigue Regime

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Synergistic Effect of Environmental Media and Stress on the Fatigue Fracture Behaviour of Aluminium Alloys

Effects of pressurized water reactor environment and cyclic loading parameters on the low cycle fatigue behavior of 304L stainless steel

Environment-induced Fatigue Cracking Behavior of Aluminum Alloys and Modification Methods