Abstract:Nanocrystalline materials have an extensive application in engineering due to their excellent performance on strength and toughness. This work carries out molecular dynamics simulation to identify the atomistic scale behaviors of crack propagation in nanocrystalline bcc iron, where the effect of grain size less than 15 nm is examined. The crack, instead of the grain boundary, is found to play a major role in the engineering stress-strain behavior. The maximum stress of the cracked model is no longer consistent with the inverse Hall-Petch relationship. Based on three-dimensional investigation, the diverse propagation behaviors on different cross sections along crack front are revealed, and the mechanism of intergranular decohesion is clarified. Through intergranular decohesion, the fast brittle cleavage on one cross section can accelerate the ductile propagation on the other cross sections. With a decrease in grain size, the intergranular decohesion effect weakens, and the crack propagation becomes more ductile. The threshold for crack ductile growth also increases with grain size decrease, which is very different from the inverse Hall-Petch relationship. The nanocrystalline iron with a small grain size has lower tensile strength but higher crack ductile growth threshold. Besides, the convictive evidence of asymmetrical propagation in nanocrystalline bcc iron is found. The asymmetrical propagation behavior is determined by the different abilities of leading partial dislocation nucleation on the asymmetrically distributed atomic close-packed planes. Since the grain orientation is random, the atoms are usually distributed asymmetrically along the crack plane. The asymmetrical behavior dominates the crack propagation inside grain for nanocrystalline bcc iron.

J-integral Evaluation of a Mode I Crack in Gradient Nanocrystalline Metals

Evaluating the J-integral of Mode I Crack in Gradient Nanocrystalline Metals with Residual Stress Induced by Surface Mechanical Treatment

Micromechanical Simulation of Fracture Behavior of Nanostructured Metals with Bimodal Grain Size Distribution

Micromechanical simulation of fracture behavior of bimodal nanostructured metals

Numerical investigation of fracture behavior of nanostructured Cu with bimodal grain size distribution

Micromechanical modeling for mechanical properties of gradient-nanotwinned metals with a composite microstructure

Modelling the Plastic Deformation of Nanostructured Metals with Bimodal Grain Size Distribution

Diffusive crack-grain interplay in freestanding nanocrystalline silver thin film

Crystal cracking of grain-gradient aluminum by a combined CPFEM-CZM method

J-Integral Evaluation for Interface Crack of Bimetal Loaded by Normal Three-Point Bending(Modeling & Simulation)

Investigation of Fracture Characterizations of Functionally Graded Materials

Simulation of Fracture of Nanocrystalline Metals

Self-Induced Internal Corrosion Stress Transgranular Cracking in Gradient-Structural Ploycrystalline Materials at High Temperature

Nanomechanics and Nanocomposites: Mechanical Behaviors

Mode I Crack Problem for A Functionally Graded Orthotropic Strip

J Integral and Cod Fracture Criteria in 40crnimo Steel under Mixed Mode I+Ii Loading

Dynamic behavior of a finite crack in the functionally graded materials

Effects of strain gradient on the mechanical behaviors of nanocrystalline materials

Investigation of A Mode Iii Crack in Functionally Graded Magnetoelectroelastic Materials

Atomistic Scale Behaviors of Crack Propagation in Nanocrystalline Bcc Iron

Study of the relationship between J-integral and COD parameters under mixed mode I + II loading in aluminum alloy Ly 12