Design of fusion equipment of pedicle of vertebrae and biomechanical study of its effect after addition polymethylmethacrylate
胡勇,杨述华,付德皓,谢辉,徐荣明,章伟文,冯建翔
DOI: https://doi.org/10.3321/j.issn:1673-8225.2004.14.042
2004-01-01
Abstract:BACKGROUND: There are several methods to restore the failure of screw fixation at present. but its efficacy is not satisfactory.OBJECTIVE: To evalnate the hiomechanical effect of hollow screws with lateral holes augmented with polymethyl methacrylate(PMMA) in strengthening the fixation to improve the stability of the screw.DESIGN: A completely randomized controlled experiment was conducted.SETTING and PARTICIPANTS: The experiment was completed in the Institute of Biomechanics and Anatomy, Tongji Medical College, Huazhong University of Science and Technology. The subjects were fresh adult cadavers(voluntarily provided by the relatives).INTERVENTIONS: A total of 32 fresh thoracolumbar vertebrae(T11-L4) of 8adult cadavers were randomdy employed in this experiment. Solid screws of 6.5mm in diameter were implanted directly into the pedicle of vertebral arch unilaterally(subgroup A), and hollow screws with lateral holes of equivalent diameter were implanted contralaterally(snbgroup B) on 10 fresh thoracolumbar vertebrae(T11-L4) . Then the screws of both subgroups were pulled out and axial pullout test (F-max) was performed (control group), and 3-5 mL PMMA was injected into the track of every screw. Five minutes later, the solid screws(subgroup C) and the hollow screws(subgoup D) were reimplanted into the initial track respectively. An hour later at room temperature,axial pullout test was employed again(restoration group). Solid screws of 6.5mm in diameter were implanted into the pedicle of vertebral arch unilaterally (subgroup E). and hollow screws with lateral holes of equivalent diameter were implanted eontralaterally(subgroup F) on other 10 fresh thoracolumbar vertebrae. A drilling hit of 3.5 mm in diameter was used to prepare track,then screwed in the pedicle screws after injecting PMMA. An hour later,axial pullout test was employed(reinforcement group), and the distribution of PMMA was observed. Periodical/Cyclic bending resistance test on hollow screws with lateral holes in pedicle of vertebral arch was performed on the rest 12 vertebrae. And three point bending test was made on 10 solid screws and 10 hollow screws with lateral holes, respectively.MAIN OUTCOME MEASURES: Axial Pull-out force, displacement,maximtun bending force.RESULTS: Axial pullout strength was (829.2 ± 220.9) N in subgroup A,(855.0±207.5) N in subgroup B. (1853.5±387.4) N in subgroup C,(1924.4 ±383.2) N in subgroup D. (1866. 1 ±431.7) N in subgroup E and (1943.3 ±535.8) N in subgroup F. No PMMA was found in the spinal canal or on the surface of pedicle of vertebral arch when PMMA was infused into the hollow screws with lateral holes, while PMMA was easily found in thc spinal canal or on the surface of the pedicle of vertebral arch in solid screws. The hollow screws with lateral holes infused with PMMA could bear more loadings or induce fewer shifts under the same loadings compared with the controls. The max loading force of the hollow solid screws with lateral holes was (2051.29 ±69.86) N, the elastic modulus was (23941.8 ±1467.4) N/mm2 and the energy absorption was (40. 1873 ± 1. 4693) J.While the max loading force of the solid screws was (2075.01 ± 117.57)N,the elastic modulus was (24991.8 ± 1962.3) N/mm2, and the energy absorption was (44. 9630 4 1. 8663) J.CONCLUSION: PMMA can increase significantly the stabilization of the screws in pedicle of vertebral arch. And no PMMA was found in the spinal canal or on the surface of pedicle of vertebral arch when PMMA was inffused into the hollow screws with lateral holes, which is suitable for the fixation of loosing screw and the repair of the wound when screws are pulled out.