Abstract:Alloying Pt with transition metals can significantly improve the catalytic properties for the oxygen reduction reaction (ORR). However, the application of Pt-transition metal alloys in fuel cells is largely limited by poor long-term durability because transition metals can easily leach. In this study, we developed a nonmetallic doping approach and prepared a P-doped Pt catalyst with excellent durability for the ORR. Carbon-supported core-shell nanoparticles with a P-doped Pt core and Pt shell (denoted as PtPx@Pt/C) were synthesized via heat-treatment phosphorization of commercial Pt/C, followed by acid etching. Compositional analysis using electron energy loss spectroscopy and X-ray photoelectron spectroscopy clearly demonstrated that Pt was enriched in the near-surface region (approximately 1 nm) of the carbon-supported core-shell nanoparticles. Owning to P doping, the ORR specific activity and mass activity of the PtP1.4@Pt/C catalyst were as high as 0.62 mA cm−2 and 0.31 mA μgPt−1, respectively, at 0.90 V, and they were enhanced by 2.8 and 2.1 times, respectively, in comparison with the Pt/C catalyst. More importantly, PtP1.4@Pt/C exhibited superior stability with negligible mass activity loss (6% after 30000 potential cycles and 25% after 90000 potential cycles), while Pt/C lost 46% mass activity after 30000 potential cycles. The high ORR activity and durability were mainly attributed to the core-shell nanostructure, the electronic structure effect, and the resistance of Pt nanoparticles against aggregation, which originated from the enhanced ability of the PtP1.4@Pt to anchor to the carbon support. This study provides a new approach for constructing nonmetal-doped Pt-based catalysts with excellent activity and durability for the ORR.

Nitrogen-doped Pt3Co Intermetallic Compound Nanoparticles: A Durable Oxygen Reduction Electrocatalyst

Atomic Platinum Anchored on Fe‐N‐C Material for High Performance Oxygen Reduction Reaction

Nitrogen and Carbon Co-Doped CoO x Nanostructures for Oxygen Reduction

Nitrogen and Carbon Co-Doped CoOx Nanostructures for Oxygen Reduction

P-Doping Strategy Increasing the Durability of PtCo Nanoparticles for the Oxygen Reduction Reaction

High Activity and Durability of Carbon-Supported Core-Shell PtPx@Pt/C Catalyst for Oxygen Reduction Reaction

N-doped Carbon-Stabilized PtCo Nanoparticles Derived from Pt@ZIF-67： Highly Active and Durable Catalysts for Oxygen Reduction Reaction

High activity and durability of carbon-supported core-shell PtP @Pt/C catalyst for oxygen reduction reaction

Catalytic Performance and Mechanism of N-Coti@Cotio3 Catalysts for Oxygen Reduction Reaction

Enhancing oxygen reduction reaction of Pt–Co/C nanocatalysts via synergetic effect between Pt and Co prepared by one-pot synthesis

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

PtNi Alloy Nanoparticles Grown in situ on Nitrogen doped Carbon for Efficient Oxygen Reduction Reaction

Pt3(CoNi) Ternary Intermetallic Nanoparticles Immobilized on N-Doped Carbon Derived from Zeolitic Imidazolate Frameworks for Oxygen Reduction

PdCoNi Alloy Nanoparticles Decorated, Nitrogen-Doped Carbon Nanotubes for Highly Active and Durable Oxygen Reduction Electrocatalysis

Collaborative Anchoring of Pt Nanoparticles and Metal Oxide Nanoparticles on N-Doped Carbon as Catalysts for Oxygen Reduction

MOF Templated Nitrogen Doped Carbon Stabilized Pt–Co Bimetallic Nanoparticles: Low Pt Content and Robust Activity Toward Electrocatalytic Oxygen Reduction Reaction

Probing the Electro-Catalytic ORR Activity of Cobalt-Incorporated Nitrogen-Doped CNTs

In Situ Nitrogen Infiltration into an Ordered Pt3Co Alloy with Sp–d Hybridization to Boost Fuel Cell Performance

Accelerated intermediate conversion through nickel doping into mesoporous Co-N/C nanopolyhedron for efficient ORR

Engineering Platinum–nickel Nano-Alloys in Hierarchically Ordered Porous Cobalt-Nitrogen-doped Carbon for Highly Efficient Electrocatalytic Oxygen Reduction

Engineering Pt Nanoparticles with Fe and N Codoped Carbon to Boost Oxygen Reduction Catalytic Performance in Acidic Electrolyte