Abstract:Developing efficient Pt‐based alloy as oxygen reduction reaction (ORR) electrocatalysts is critical for practical applications of fuel cells. High‐temperature reduction technology can improve the alloy atoms ordering but inevitably accelerate metal sintering. Here, Pt–Ni nanoparticles (<5 nm) embedded into ordered mesoporous carbon (OMC) matrix are developed, and its confinement effect suppresses nanoparticles sintering up to 900 °C. After an elaborative dealloying process, the surface structure of Pt–Ni nanoparticles changes from a Ni‐rich to Pt‐rich layer (the thickness is about 0.15 nm). The optimized sample (PtNi3@OMC‐A) displays outstanding mass and specific activities of 2.11 A mgPt–1 and 3.23 mA cmPt–2, more than one order of magnitude higher than commercial Pt/C (20 wt%). PtNi3@OMC‐A also exhibits long‐term stability with a negligible activity loss after 10 000 potential cycles. Both experimental results and density functional theory calculations reveal that alloying effect as well as strain effect weaken Pt–O binding strength, thus resulting in an outstanding ORR activity. Furthermore, the high long‐term stability can be attributed to the confinement of OMC, inhibiting the detachment or agglomeration of the embedded alloy nanoparticles. Pt–Ni nanoparticles (≈5 nm) embedded into ordered mesoporous carbon (OMC) is synthesized via high‐temperature reduction technology. The confinement effect of OMC can suppress nanoparticles sintering up to 900 oC. Both alloying effect and strain effect weaken Pt–O binding strength and accelerate the desorption of oxygenated species on the sample surface, thus resulting in an outstanding ORR performance.

PtNi Alloy Nanoparticles Grown in situ on Nitrogen doped Carbon for Efficient Oxygen Reduction Reaction

PtNi Alloy Nanoparticles Grown in Situ on Nitrogen Doped Carbon for the Efficient Oxygen Reduction Reaction.

Shaped Pt-Ni Nanocrystals with an Ultrathin Pt-enriched Shell Derived from One-Pot Hydrothermal Synthesis As Active Electrocatalysts for Oxygen Reduction

Atomic Platinum Anchored on Fe‐N‐C Material for High Performance Oxygen Reduction Reaction

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Nodal PtNi Nanowires with Pt Skin and Controllable Near-Surface Composition for Enhanced Oxygen Reduction Electrocatalysis in Fuel Cells

High‐Temperature Confinement Synthesis of Supported Pt–Ni Nanoparticles for Efficiently Catalyzing Oxygen Reduction Reaction

One-Step Synthesized Pt-on-NiCo Nanostructures for Oxygen Reduction with High Activity and Long-Term Stability

Trimetallic Pt–Pd–Ni Octahedral Nanocages with Subnanometer Thick-Wall Towards High Oxygen Reduction Reaction

PdCoNi Alloy Nanoparticles Decorated, Nitrogen-Doped Carbon Nanotubes for Highly Active and Durable Oxygen Reduction Electrocatalysis

Ultrathin Ni–N–C layer modified Pt–Ni alloy nanoparticle catalysts for enhanced oxygen reduction

Synthesis and Design of a Highly Stable Platinum Nickel Electrocatalyst for the Oxygen Reduction Reaction

Enhanced Electrocatalytic Performance of Ultrathin PtNi Alloy Nanowires for Oxygen Reduction Reaction

Scalable Nanoporous (Pt1-Xnix)3al Intermetallic Compounds As Highly Active and Stable Catalysts for Oxygen Electroreduction.

Engineering Pt Nanoparticles with Fe and N Codoped Carbon to Boost Oxygen Reduction Catalytic Performance in Acidic Electrolyte

Atomically Dispersed Ni-N4 Sites Assist Pt3 Ni Nanocages with Pt Skin to Synergistically Enhance Oxygen Reduction Activity and Stability

Collaborative Anchoring of Pt Nanoparticles and Metal Oxide Nanoparticles on N-Doped Carbon as Catalysts for Oxygen Reduction

Facile Aqueous Phase Synthesis of Carbon Supported B-doped Pt3Ni Nanocatalyst for Efficient Oxygen Reduction Reaction

Ultrasmall PtNi Bimetallic Nanoclusters for Oxygen Reduction Reaction in Alkaline Media

Octahedral Pd@Pt1.8Ni Core-Shell Nanocrystals with Ultrathin PtNi Alloy Shells As Active Catalysts for Oxygen Reduction Reaction.

A One‐step Way to Novel Carbon‐niobium Nitride Nanoparticles for Efficient Oxygen Reduction