Abstract:To explore efficient non-noble metal-based electrocatalysts for oxygen reduction reaction (ORR), herein we developed a facile bottom-up approach for the fabrication of a hollow porous carbon sphere codoped with ultrasmall Co nanoparticles and uniform nitrogen distribution (Co-HNCS) via one-step pyrolysis of a core-shell type precursor composing of polystyrene (PS) core and bimetallic ZIF (zeolite imidazolate framework) shell. The bimetallic Co-Zn-ZIFs (BMZIFs) was selected as the sacrifice template due to not only its high nitrogen content and regular porosity but also the superiority that Zn species in BMZIFs can both spatially separate Co species to suppress the aggregation of ultra-small Co NPs and be evaporated to afford extra pores during high-temperature pyrolysis. As expected, by adjusting the starting molar ratio of Zn to Co, we were able to prepare Co-HNCS-x (x represent the molar ratio of Co to total starting metal feeding) that exhibited unique hollow structure with large surface areas, enhanced mass transport, high porosities, tunable particle sizes and graphitization degrees, abundant highly active CoNx sites, and thus significantly improved ORR performance. Particularly, the optimal Co-HNCS-0.2 exhibited the remarkable ORR activity (the onset and half-wave potentials were 0.94 and 0.82 V vs. RHE, respectively) via an efficient four-electron-dominant ORR process in alkaline medium, which outperformed that of commercial Pt/C (20 wt%, the onset and half-wave potentials were 0.93 and 0.80 V vs. RHE, respectively) and most of previously reported Co-based catalysts. Moreover, it also displayed much superior stability and tolerance to methanol as compared to Pt/C, further highlighting the merit of this facile synthesis approach. Our findings might inspire new thoughts on the development of precious-metal-free, highly-efficient and cost-effective ORR electrocatalysts derived from MOF.

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

Hollow Porous Carbon-Confined Atomically Ordered PtCo3 Intermetallics for an Efficient Oxygen Reduction Reaction

Coupling Atomically Ordered PtCo Catalysts with Ultrathin Nitrogen-Doped Carbon Shell for Enhanced Oxygen Reduction

Synergizing Amino Tethering and Carbon Shell Confinement Enables Confinement Synthesis of PtCo Intermetallic Catalysts for Highly Durable Fuel Cells

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

The Quasi‐Pt‐Allotrope Catalyst: Hollow PtCo@single‐Atom Pt1 on Nitrogen‐Doped Carbon Toward Superior Oxygen Reduction

PtCo Incorporated Porous Carbon Nanofiber As a Promising Oxygen Reduction Electrocatalyst

N-doped Carbon Confined Ternary Pt2NiCo Intermetallics for Efficient Oxygen Reduction Reaction

Co@C Nanoparticle Embedded Hierarchically Porous N-Doped Hollow Carbon for Efficient Oxygen Reduction

Electrochemical Synthesis of Monodispersed and Highly Alloyed PtCo Nanoparticles with a Remarkable Durability Towards Oxygen Reduction Reaction

Carbon-Supported Mn-Doped Intermetallic Ptco As an Efficient Nanocatalyst for the Oxygen Reduction Reaction

Rational Design of Hierarchical Porous Cobalt, Nitrogen-doped Carbon Architectures as Efficient Oxygen Reduction Reaction Electrocatalysts.

Rational Design of Hollow N/Co-doped Carbon Spheres from Bimetal-Zifs for High-Efficiency Electrocatalysis

Nitrogen-doped Pt3Co Intermetallic Compound Nanoparticles: A Durable Oxygen Reduction Electrocatalyst

Doped Porous Carbon Nanostructures with N Co O Catalytic Active Sites for Efficient Electrocatalytic Oxygen Reduction Reaction

Structurally Ordered Low‐Pt Intermetallic Electrocatalysts Toward Durably High Oxygen Reduction Reaction Activity

Highly Efficient PtCo Nanoparticles on Co–N–C Nanorods with Hierarchical Pore Structure for Oxygen Reduction Reaction

Ordered Mesoporous Carbon Confined Highly Dispersed PtCo Alloy for the Oxygen Reduction Reaction: the Effect of Structure and Composition on Performance

Core-shell Co/CoNx@C Nanoparticles Enfolded by Co-N Doped Carbon Nanosheets As a Highly Efficient Electrocatalyst for Oxygen Reduction Reaction

Highly Dispersed Pt3Co Nanocatalysts Embedded in Porous Hollow Carbon Spheres with Efficient Electrocatalytic O2-Reduction and H2-Evolution Activities

Efficient ORR Activity of N-doped Porous Carbon Encapsulated Cobalt Electrocatalyst Derived from a Novel Bimetal-Organic Framework