Abstract:In this article, the original Li1.2Mn0.54Ni0.13Co0.13O2 lithium-rich manganese-based cathode material with a uniform distribution of polygonal prisms was synthesized by a simple and reproducible sol-gel method, followed by a simple chemical deposition method. The structure and electrochemical performance of the original and modified cathode materials were characterized by XRD, XPS, EDS, SEM, TEM, and constant current charge/discharge tests. The results showed that LaF3 was uniformly coated on the surface of the original material and the thickness of the 2 wt% coating layer was about 2-3 nm. With this coating amount, the cathode material could obtain the best cycling and rate performance. The first coulomb efficiency of the modified material was 73%, which was 7% higher than that of the original material. Secondly, the cycling performance was improved. When the coated material was cycled at 0.2 C for 50 cycles, the discharge capacity was 325mAh∙g-1, and the capacity retention rate was 99.21%, while the original material was only 78.73%. Finally, the performance was also improved at high current density. The coated material could still reach 170mAh∙g-1 at 5C, which was 70% higher than the original material. The significant improvement in electrochemical performance was attributed to the fact that the LaF3 coating layer made the material avoid direct contact with the electrolyte which could reduce the occurrence of side reactions and increase the stability of the material. Besides, expanded layer space resulted from lattice expansion after coating could broaden the transmission channel of lithium ions and facilitate the insertion-extraction of lithium ions during charge and discharge.

Novel LaFeO3 Coating Modification for a LiFePO4 Cathode

Mixed Lithium Ion and Electron Conducting LiAlPO 3.93 F 1.07 -Coated LiCoO 2 Cathode with Improved Electrochemical Performance

Enhance electrochemical performance of LiFePO4 cathode material by Al-doped Li7La3Zr2O12 and carbon co-coating surface modification

Improved Electrochemical Performance of LaF3-coated Layered Oxide Li1.2Mn0.54Ni0.13Co0.13O2 Cathode Material for Lithium- Ion Batteries Prepared by Sol-Gel Method

Improving the Cycling Stability and Rate Capability of LiMn0.5Fe0.5PO4/C Nanorod As Cathode Materials by LiAlO2 Modification

Fluorine doped carbon coating of LiFePO4 as a cathode material for lithium-ion batteries

Improving rate performance of LiFePO4 cathode materials by hybrid coating of nano-Li3PO4 and carbon

Three-Dimensional Carbon-Coated LiFePO4 Cathode with Improved Li-Ion Battery Performance

Surface Modification Engineering Enabling LiMn x Fe1‐ x PO4 Cathode Against Aggressive Cathode Chemistries for Excellent Performance Lithium‐ion batteries

Enhancing the Power Capability of Lithium-Rich Manganese-Based Layered Oxide Cathodes by LaF3 Modification

Enhanced Electrochemical Performance of LiFePO4 Originating from the Synergistic Effect of ZnO and C Co-Modification

Optimization of Carbon Coatings on LiFePO4: Carbonization Temperature and Carbon Content

Synergistic structure of LiFeO2 and Fe2O3 layers with electrostatic shielding effect to suppress surface lattice oxygen release of Ni-rich cathode

Enhanced prelithiation performance of Li 5 FeO 4 cathode additive and optimized solid electrolyte interface enabled by Mn substitution

Fabrication of FePO 4 layer coated LiNi 1 / 3 Co 1 / 3 Mn 1 / 3 O 2 : Towards high-performance cathode materials for lithium ion batteries

Based on N, F, and P co-doping biomass carbon to construct 3D porous carbon coated LiFePO4 for preparing lithium-ion batteries

Enhanced Electrochemical Property of FePO4-coated LiNi0.5Mn1.5O4 As Cathode Materials for Li-ion Battery

Fluorine Doping and Al2O3 Coating Co-modified Li[Li0.20Ni0.133Co0.133Mn0.534]O2 As High Performance Cathode Material for Lithium-Ion Batteries

Effect of carbon coating on the electrochemical performance of LiFePO4/C as cathode materials for aqueous electrolyte lithium-ion battery

Structure and Electrochemical Performance of LiFePO4/C Cathode Materials Coated with Nano Al2O3 for Lithium-ion Battery

Synthesis, characterization and properties of LiFePO4/C cathode material